Instrumented Impact and Static Indentation of Composites
作者： Shaw Ming Lee , Paul Zahuta
DOI: 10.1177/002199839102500205
关键词: Indentation 、 Impact test 、 Fiber 、 Low speed 、 Delamination 、 Impact 、 Composite material 、 Materials science 、 Energy absorption 、 Fracture toughness
摘要: … damage caused the force to level off. There was evidence … not significantly affect the nU trends. The observed variation of … localized, fiber breakage could become more severe in a …
sagepub.com
harvard.edu
sci-hub.se 参考文章(6)
JG Williams, MD Rhodes, Effect of resin on impact damage tolerance of graphite/epoxy laminates ASTM International. ,(1982) , 10.1520/STP28495S
D. J. Boll, W. D. Bascom, J. C. Weidner, W. J. Murri, A microscopy study of impact damage of epoxy-matrix carbon-fibre composites Journal of Materials Science. ,vol. 21, pp. 2667- 2677 ,(1986) , 10.1007/BF00551471
Peter O. Sjoblom, J. Timothy Hartness, Tobey M. Cordell, On Low-Velocity Impact Testing of Composite Materials Journal of Composite Materials. ,vol. 22, pp. 30- 52 ,(1988) , 10.1177/002199838802200103
T. OBRIEN, E. GUYNN, The influence of lay-up and thickness on composite impact damage and compression strength 26th Structures, Structural Dynamics, and Materials Conference. ,(1985) , 10.2514/6.1985-646
Composite Materials: Testing and Design (6th Conference) ASTM International. ,(1982) , 10.1520/STP787-EB
A. E. Johnson, D. R. Moore, R. S. Prediger, P. E. Reed, S. Turner, The falling weight impact test applied to some glass-fibre reinforced nylons: Part 1 Appraisal of the method Journal of Materials Science. ,vol. 21, pp. 3153- 3161 ,(1986) , 10.1007/BF00553351