Silicon-oxygen equilibrium and nitrogen distribution between CaO−SiO2 slags and liquid iron
作者： Ryo Inoue , Hideaki Suito
DOI: 10.1007/BF02649721
关键词: Distribution (mathematics) 、 Silicon oxygen 、 Chemistry 、 Mineralogy 、 Metallic materials 、 Nitrogen 、 Liquid iron 、 Analytical chemistry 、 Molten slag
摘要: Silicon-oxygen equilibria in an Fe-0.003 ~ 27 mass pct Si alloy equilibrium with the CaO-SiO2 slags were studied temperature range of 1823 to 1923 K using a lime crucible. At same time, nitrogen distribution ratios, LN, between slag and metal measured, from these results reported values for activities SiO2, nitride capacities, % MathType!MTEF!2!1!+-% feaafiart1ev1aaatCvAUfKttLearuqr1ngBPrgarmWu51MyVXgatC% vAUfeBSjuyZL2yd9gzLbvyNv2CaeHbd9wDYLwzYbItLDharyavP1wz% ZbItLDhis9wBH5garqqtubsr4rNCHbGeaGqiVy0df9qqqrpepC0xbb% L8F4rqqrFfpeea0xe9Lq-Jc9vqaqpepm0xbba9pwe9Q8fs0-yqaqpe% pae9pg0FirpepeKkFr0xfr-xfr-xb9adbaqaaeGaciGaaiaabeqaam% aaeaqbaaGcbaaceiGaa83qamaaBaaaleaaiqaacaGFobWaaWbaaWqa% beaacaGFZaGaeyOeI0caaaWcbeaaaaa!3DDE! $$C_{N^{3 - } $$ , defined by (mass N). aaeaqbaaGcbaWaaSGbaeaacqWGqbaudaqhaaWcbaacbaGae83ta80a% aSbaaWqaaGabaiaa+jdaaeqaaaWcbaWaaSGbaeaacaGFZaaabaGaa4% hnaaaaaaaakeaacqWGqbaudaqhaaWcbaGae8Nta40aaSbaaWqaaiaa% +jdaaeqaaaWcbaWaaSGbaeaacaGFXaaabaGaa4Nmaaaaaaaaaaaa!441C! $${{P_{O_2 }^{{3 \mathord{\left/ {\vphantom {3 4}} \right. \kern-\nulldelimiterspace} {{P_{O_2 {P_{N_2 }^{{1 {1 2}} }}} }}$$ evaluated. It was found that LN decreased, whereas those for increased increase temperature. Activities SiO2 determined and obtained previous gas-slag experiments. These compared results.
springer.com
harvard.edu
elsevier.com
sci-hub.se 参考文章(14)
E. T. Turkdogan, Physical chemistry of high temperature technology ,(1980)
D. A. R. Kay, J. Taylor, Activities of silica in the lime + alumina + silica system Transactions of The Faraday Society. ,vol. 56, pp. 1372- 1386 ,(1960) , 10.1039/TF9605601372
G. K. Sigworth, J. F. Elliott, The Thermodynamics of Liquid Dilute Iron Alloys Metal science. ,vol. 8, pp. 298- 310 ,(1974) , 10.1179/MSC.1974.8.1.298
R. J. Fruehan, Activities in liquid Fe-V-O and Fe-B-O alloys Metallurgical Transactions. ,vol. 1, pp. 2083- 2088 ,(1970) , 10.1007/BF02643418
Hideaki Suito, Hajime Inoue, Ryo Inoue, Aluminium-Oxygen Equilibrium between CaO-Al2O3 Melts and Liquid Iron Isij International. ,vol. 31, pp. 1381- 1388 ,(1991) , 10.2355/ISIJINTERNATIONAL.31.1381
Ryo Inoue, Hajime Inoue, Hideaki Suito, Partitions of Nitrogen and Sulfur between CaO-Al2O3 Melts and Liquid Iron Isij International. ,vol. 31, pp. 1389- 1395 ,(1991) , 10.2355/ISIJINTERNATIONAL.31.1389
Katsutomo Tomioka, Hideaki Suito, NITRIDE CAPACITY OF CAO-AL2O3 MELTS Isij International. ,vol. 31, pp. 1316- 1321 ,(1991) , 10.2355/ISIJINTERNATIONAL.31.1316
Kimihisa Ito, R. J. Fruehan, Thermodynamics of nitrogen in CaO-SiO2-AI2O3 slags and its reaction with Fe-Csat. melts Metallurgical Transactions B. ,vol. 19, pp. 419- 425 ,(1988) , 10.1007/BF02657739
H. Suito, T. Kozono, Thermodynamics of nitrogen in BaO−Al2O3 and BaO−SiO2−Al2O3 melts Ironmaking & Steelmaking. ,vol. 19, pp. 145- 151 ,(1992)
Katsutomo Tomioka, Hideaki Suito, Nitride capacities in CaO–SiO2 and CaO–SiO2–Al2O3 melts Steel Research. ,vol. 63, pp. 1- 6 ,(1992) , 10.1002/SRIN.199200459