Temperature rise at a dislocation pile-up breakthrough
作者： R.W. Armstrong , W.L. Elban
DOI: 10.1016/0921-5093(89)90642-4
关键词: Forensic engineering 、 Dislocation 、 Aluminium 、 Pile 、 Materials science 、 Composite material 、 Explosive material
摘要: Abstract Relatively large temperature rises are theoretically estimated for collapsing dislocation pile-ups in MgO, the explosive RDX (cyclotrimethylenetrinitramine) and LiF, as compared with α-Ti α-Fe, where localized heating effects known to be important much larger than those which can occur aluminum.
elsevier.com
sci-hub.se 参考文章(5)
N. M. Madhava, R. W. Armstrong, Discontinuous twinning of titanium at 4.2 K Metallurgical Transactions. ,vol. 5, pp. 1517- 1519 ,(1974) , 10.1007/BF02646644
R.W. Armstrong, C.S. Coffey, W.L. Elban, Adiabatic heating at a dislocation pile-up avalanche Acta Metallurgica. ,vol. 30, pp. 2111- 2116 ,(1982) , 10.1016/0001-6160(82)90131-6
R.W. Armstrong, W.L. Elban, Cracking at hardness nicro-indentations in RDX explosive and MgO single crystals Materials Science and Engineering: A. ,vol. 111, pp. 35- 43 ,(1989) , 10.1016/0921-5093(89)90195-0
J.D. Eshelby, P.L. Pratt, Note on the heating effect of moving dislocations Acta Metallurgica. ,vol. 4, pp. 560- 562 ,(1956) , 10.1016/0001-6160(56)90056-6
J. C. M. Li, Y. T. Chou, The role of dislocations in the flow stress grain size relationships Metallurgical and Materials Transactions B. ,vol. 1, pp. 1145- 1159 ,(1970) , 10.1007/BF02900225