Modeling of Damage Development During Sintering of Ceramics
作者： A. Maximenko , O. Van Der Biest , E. Olevsky
关键词: Composite material 、 Materials science 、 Macroscopic model 、 Fissure 、 Ceramic 、 Sintering
摘要: Sintering of powder-based ceramic composites is often accompanied by developments cracks or large pores. As a rule, damage development active only at early stage sintering when junctures between particles are not strong enough. A macroscopic model taking into account broken put forward. The follows both densification and during sintering.
springer.com
sci-hub.se 参考文章(3)
F. F. LANGE, M. METCALF, Processing‐Related Fracture Origins: II, Agglomerate Motion and Cracklike Internal Surfaces Caused by Differential Sintering Journal of the American Ceramic Society. ,vol. 66, pp. 398- 406 ,(1983) , 10.1111/J.1151-2916.1983.TB10069.X
Peter Z. Cai, David J. Green, Gary L. Messing, Constrained Densification of Alumina/Zirconia Hybrid Laminates, I: Experimental Observations of Processing Defects Journal of the American Ceramic Society. ,vol. 80, pp. 1929- 1939 ,(2005) , 10.1111/J.1151-2916.1997.TB03075.X
C.P. Ostertag, P.G. Charalambides, A.G. Evans, Observations and analysis of sintering damage Acta Metallurgica. ,vol. 37, pp. 2077- 2084 ,(1989) , 10.1016/0001-6160(89)90093-X