Influence of oxide films on primary water stress corrosion cracking initiation of alloy 600
作者： J. Panter , B. Viguier , J.-M. Cloué , M. Foucault , P. Combrade
DOI: 10.1016/J.JNUCMAT.2005.10.002
关键词: Metallurgy 、 Stress corrosion cracking 、 Corrosion 、 Alloy 、 Stress (mechanics) 、 Grain boundary 、 Materials science 、 Intergranular corrosion 、 Oxide 、 Chromium
摘要: … , a mechanism for stress corrosion crack initiation of alloy 600 in PWR primary water was … Lewis, GL Makar, Prediction of PWSCC in nickel base alloys using crack growth rate models, In…
harvard.edu
archives-ouvertes.fr
elsevier.com
sci-hub.se 参考文章(19)
Stephane Gardey, Etude de la corrosion generalisee des alliages 600, 690 et 800 en milieu primaire. Contribution a la comprehension des mecanismes Paris 6. ,(1998)
Stephen M. Bruemmer, Edward P. Simonen, Larry E. Thomas, Diffusion Kinetic Issues During Intergranular Corrosion of Ni-Base Alloys Corrosion. ,(2000)
WR Catlin, DC Lord, TA Prater, LF Coffin, The Reversing D-C Electrical Potential Method ASTM International. ,(1985) , 10.1520/STP32880S
R. W. Staehle, Z. Fang, Comments on a Proposed Mechanism of Internal Oxidation for Alloy 600 as Applied to Low Potential SCC Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors. pp. 69- 78 ,(2013) , 10.1002/9781118787618.CH7
J. Panter, Bernard Viguier, Eric Andrieu, Microstructure evolution of alloy 600 during dry oxidation Materials Science Forum. pp. 141- 148 ,(2001) , 10.4028/WWW.SCIENTIFIC.NET/MSF.369-372.141
Robert A. Johnson, Nghi Q. Lam, Solute segregation in metals under irradiation Physical Review B. ,vol. 13, pp. 4364- 4375 ,(1976) , 10.1103/PHYSREVB.13.4364
Ph. Berge, Corrosion intergranulaire d'un alliage dutype Inconel 600 dans la vapeur d'eau Corrosion Science. ,vol. 10, pp. 185- 189 ,(1970) , 10.1016/S0010-938X(70)80077-4
R. H. Bricknell, D. A. Woodford, The embrittlement of nickel following high temperature air exposure Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 12, pp. 425- 433 ,(1981) , 10.1007/BF02648539
F. Carrette, M. C. Lafont, G. Chatainier, L. Guinard, B. Pieraggi, Analysis and TEM examination of corrosion scales grown on Alloy 690 exposed to pressurized water at 325 °C Surface and Interface Analysis. ,vol. 34, pp. 135- 138 ,(2002) , 10.1002/SIA.1269
Simon Perusin, Bernard Viguier, Daniel Monceau, Eric Andrieu, Experimental Study of the Interactions between Oxidation and Structural Defects Materials Science Forum. pp. 123- 130 ,(2004) , 10.4028/WWW.SCIENTIFIC.NET/MSF.461-464.123