Templating of Metal Oxides by Electrodeposition
作者： Maik Rudolf Johann Scherer
DOI: 10.1007/978-3-319-00354-2_5
关键词: Inorganic chemistry 、 Oxide 、 Metal hydroxide 、 Mesoporous material 、 Materials science 、 Transition metal 、 Dissolution 、 Chemical engineering 、 Surface-area-to-volume ratio 、 Thin film 、 Intercalation (chemistry)
摘要: The aim of this part the study was to use voided DG films, typically prepared from for template-assisted electrodeposition nanostructured transition metal oxide (MO) or hydroxide thin films. MOs are commonly utilized their catalytic activity, intercalation and semi-conductive properties. Nanostructuring these is believed enhanced unique material properties by providing a large active area simultaneous improving access bulk material. Subsequent deposition MO selective removal organic scaffold dissolution yields desired mesoporous network, which characterized high surface volume ratio, ideal many nanotechnology applications, see Fig. 5.1.
springer.com
sci-hub.st 参考文章(66)
David R. Rosseinsky, Paul M. S. Monk, Roger J. Mortimer, Electrochromism and Electrochromic Devices ,(2007)
Claes-Göran Granqvist, Handbook of inorganic electrochromic materials ,(1995)
Katsunori Takahashi, Ying Wang, Guozhong Cao, Growth and electrochromic properties of single-crystal V2O5 nanorod arrays Applied Physics Letters. ,vol. 86, pp. 053102- ,(2005) , 10.1063/1.1857087
Grace Wee, Huan Zhong Soh, Yan Ling Cheah, Subodh G. Mhaisalkar, Madhavi Srinivasan, Synthesis and electrochemical properties of electrospun V2O5 nanofibers as supercapacitor electrodes Journal of Materials Chemistry. ,vol. 20, pp. 6720- 6725 ,(2010) , 10.1039/C0JM00059K
Th. Pauporté, A. Goux, A. Kahn-Harari, N. de Tacconi, C.R. Chenthamarakshan, K. Rajeshwar, D. Lincot, Cathodic electrodeposition of mixed oxide thin films Journal of Physics and Chemistry of Solids. ,vol. 64, pp. 1737- 1742 ,(2003) , 10.1016/S0022-3697(03)00122-7
Zheng Chen, Veronica Augustyn, Jing Wen, Yuewei Zhang, Meiqing Shen, Bruce Dunn, Yunfeng Lu, High-performance supercapacitors based on intertwined CNT/V2O5 nanowire nanocomposites. Advanced Materials. ,vol. 23, pp. 791- 795 ,(2011) , 10.1002/ADMA.201003658
Torsten Brezesinski, John Wang, Sarah H. Tolbert, Bruce Dunn, Ordered mesoporous [alpha]-MoO3 with iso-oriented nanocrystalline walls for thin-film pseudocapacitors Nature Materials. ,vol. 9, pp. 146- 151 ,(2010) , 10.1038/NMAT2612
I. Bouessay, A. Rougier, P. Poizot, J. Moscovici, A. Michalowicz, J.-M. Tarascon, Electrochromic degradation in nickel oxide thin film: A self-discharge and dissolution phenomenon Electrochimica Acta. ,vol. 50, pp. 3737- 3745 ,(2005) , 10.1016/J.ELECTACTA.2005.01.020
Hee Y. Lee, J.B. Goodenough, Ideal Supercapacitor Behavior of Amorphous V2O5·nH2O in Potassium Chloride (KCl) Aqueous Solution Journal of Solid State Chemistry. ,vol. 148, pp. 81- 84 ,(1999) , 10.1006/JSSC.1999.8367
G. Helen Annal Therese, P. Vishnu Kamath, Electrochemical Synthesis of Metal Oxides and Hydroxides Chemistry of Materials. ,vol. 12, pp. 1195- 1204 ,(2000) , 10.1021/CM990447A