Injection molding of zirconia oxygen sensor thimbles by an aqueous process

作者： Joan V. Burlew , Gary B. Marsh , Anthony J. Fanelli , Clifford P. Ballard

DOI:

关键词: Powder mixture 、 Oxygen sensor 、 Cubic zirconia 、 Particle size 、 Ceramic 、 Molding (process) 、 Sintering 、 Micrometre 、 Inorganic chemistry 、 Materials science 、 Composite material

摘要: A ceramic element of a zirconia oxygen sensor is shaped from powder mixture. The mixture, comprising having an average particle size less than or equal to 1 micrometer, gel-forming material and gel forming solvent, molded at temperature pressure sufficient produce the density least 5.5 g/cm3.

google.com 本地加速

freepatentsonline.com 本地加速

osti.gov 本地加速

google.ch LINK 下载加速

lens.org UNKNOWN 下载加速

freepatentsonline.com UNKNOWN 下载加速

参考文章(7)

Ronald D. Rivers, Method of injection molding powder metal parts ,(1976)

James E. Schuetz, Method of preparing an aqueous inorganic powder slurry which is extruded and dried to form an inorganic article ,(1988)

Denton R Wieland, Bobby L Woods, Cement preflush method ,(1974)

Robert A. Pett, S. Burhan A. Qaderi, V. Durga N. Rao, Moldable mixture of sacrificial binder and sinterable particulate solids ,(1979)

Frans Heffels, Jan Karel Pieterse, Willibrordus Marie Gertrud Franciscus Pontenagel, Cornelis Wilhelmus Maria Bastiaansen, Thin self-supporting inorganic green compacts and process for the preparation of such green compacts ,(1990)

Robert Dean Silvers, Anthony Joseph Fanelli, Aqueous compositions for injection moulding comprising a gel-forming material and ceramic and/or metal powder ,(1987)

Shigeo Soejima, Syunzo Mase, A method of producing ceramics ,(1984)