Extension of the Unified Approach to fatigue crack growth to environmental interactions
作者： K Sadananda , A.K Vasudevan , R.L Holtz
DOI: 10.1016/S0142-1123(01)00137-2
关键词: Fatigue testing 、 Fracture mechanics 、 Materials science 、 Extension (predicate logic) 、 Corrosion fatigue 、 Paris' law 、 Structural engineering
摘要: … values for a given material, microstructure and environment, ΔK * and … We can state that true corrosion fatigue occurs when(1a) [{(da/dN) EF −… Fracture mechanics and corrosion fatigue …
elsevier.com
sci-hub.se 
researchgate.net 参考文章(10)
J. Bressers, Fatigue and Microstructure Springer, Dordrecht. pp. 385- 410 ,(1987) , 10.1007/978-94-009-1347-9_39
G. A. Webster, R. A. Ainsworth, Creep—fatigue crack growth High Temperature Component Life Assessment. pp. 175- 247 ,(1994) , 10.1007/978-94-017-1771-7_6
John Gittus, Cavities and cracks in creep and fatigue Applied Science. ,(1981)
Arthur J. McEvily, Fracture Mechanics and Corrosion Fatigue ASTM International. ,(1972) , 10.1520/STP44804S
J. C. Newman, Wolf Elber, Mechanics of Fatigue Crack Closure ,(1988)
S. Suresh, Fatigue of materials ,(1991)
R.A. Oriani, P.H. Josephic, Equilibrium aspects of hydrogen-induced cracking of steels Acta Metallurgica. ,vol. 22, pp. 1065- 1074 ,(1974) , 10.1016/0001-6160(74)90061-3
R. P. Wei, G. W. Simmons, Recent progress in understanding environment assisted fatigue crack growth International Journal of Fracture. ,vol. 17, pp. 235- 247 ,(1981) , 10.1007/BF00053522
N. Louat, K. Sadananda, M. Duesbery, A. K. Vasudevan, A theoretical evaluation of crack closure Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 24, pp. 2225- 2232 ,(1993) , 10.1007/BF02648597