Longitudinal Crack Initiation Under Pure Rolling Contact Fatigue
作者： W. Cheng , H. S. Cheng , L. M. Keer
DOI: 10.1080/10402009408983265
关键词: Forensic engineering 、 Crack initiation 、 Materials science 、 Composite material 、 Rolling contact fatigue
摘要: Pure rolling contact fatigue tests were carried out on a two-disc machine. The longitudinal cracks initiated the specimen surface with pure and rough driving disc conditions. Cracks...
sci-hub.se 参考文章(6)
W. Holzhauer, Surface Changes Around Large Raceway Indentations During Run-in of Tapered Roller Bearings Tribology Transactions. ,vol. 34, pp. 361- 368 ,(1991) , 10.1080/10402009108982045
Norimune Soda, Takashi Yamamoto, Effect of Tangential Traction and Roughness on Crack Initiation/Propagation During Rolling Contact Tribology Transactions. ,vol. 25, pp. 198- 206 ,(1982) , 10.1080/05698198208983081
R. Gohar, A. Cameron, The Mapping of Elastohydrodynamic Contacts Tribology Transactions. ,vol. 10, pp. 215- 225 ,(1967) , 10.1080/05698196708972181
W. E. Littmann, R. L. Widner, Propagation of Contact Fatigue From Surface and Subsurface Origins Journal of Basic Engineering. ,vol. 88, pp. 624- 635 ,(1966) , 10.1115/1.3645922
B. J. Hamrock, D. Dowson, Isothermal Elastohydrodynamic Lubrication of Point Contacts: Part III—Fully Flooded Results Journal of Lubrication Technology. ,vol. 99, pp. 264- 275 ,(1977) , 10.1115/1.3453074
R. S. Zhou, H. S. Cheng, T. Mura, Micropitting in Rolling and Sliding Contact Under Mixed Lubrication Journal of Tribology-transactions of The Asme. ,vol. 111, pp. 605- 613 ,(1989) , 10.1115/1.3261984