Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles
作者： Shukai Cheng , Zhonghe Shui , Xu Gao , Jianxin Lu , Tao Sun
DOI: 10.1016/J.CEMCONCOMP.2020.103629
关键词: Materials science 、 Chemical engineering 、 Wetting 、 Chloride 、 Porosity 、 Magnesium 、 Diffusion 、 Portland cement 、 Portlandite 、 Mortar
摘要: … degradation mechanisms of Portland cement mortar exposed to seawater attack together with drying-wetting … The reason is explained by that the sulfate attack results in the formation of …
researchgate.net 
sci-hub.st 参考文章(57)
Natalya Shanahan, Abla Zayed, Cement composition and sulfate attack: Part I Cement and Concrete Research. ,vol. 37, pp. 618- 623 ,(2007) , 10.1016/J.CEMCONRES.2006.12.004
Z. Makhloufi, S. Aggoun, B. Benabed, E.H. Kadri, M.Bederina, Effect of magnesium sulfate on the durability of limestone mortars based on quaternary blended cements Cement & Concrete Composites. ,vol. 65, pp. 186- 199 ,(2016) , 10.1016/J.CEMCONCOMP.2015.10.020
Ueli Angst, Bernhard Elsener, Claus K. Larsen, Øystein Vennesland, Critical Chloride Content in Reinforced Concrete: A Review Cement and Concrete Research. ,vol. 39, pp. 1122- 1138 ,(2009) , 10.1016/J.CEMCONRES.2009.08.006
N.R. Buenfeld, J.B. Newman, The development and stability of surface layers on concrete exposed to sea-water Cement and Concrete Research. ,vol. 16, pp. 721- 732 ,(1986) , 10.1016/0008-8846(86)90046-3
K. Sotiriadis, E. Nikolopoulou, S. Tsivilis, Sulfate resistance of limestone cement concrete exposed to combined chloride and sulfate environment at low temperature Cement & Concrete Composites. ,vol. 34, pp. 903- 910 ,(2012) , 10.1016/J.CEMCONCOMP.2012.05.006
Minghua Zhang, Jiankang Chen, Yunfeng Lv, Dongjie Wang, Jian Ye, Study on the expansion of concrete under attack of sulfate and sulfate–chloride ions Construction and Building Materials. ,vol. 39, pp. 26- 32 ,(2013) , 10.1016/J.CONBUILDMAT.2012.05.003
G.K Glass, R Yang, T Dickhaus, N.R Buenfeld, Backscattered electron imaging of the steel–concrete interface Corrosion Science. ,vol. 43, pp. 605- 610 ,(2001) , 10.1016/S0010-938X(00)00146-3
M. Frias, S. Goñi, R. García, R. Vigil de La Villa, Seawater effect on durability of ternary cements. Synergy of chloride and sulphate ions Composites Part B-engineering. ,vol. 46, pp. 173- 178 ,(2013) , 10.1016/J.COMPOSITESB.2012.09.089
S.E. Hussain, Rasheeduzzafar, A. Al-Musallam, A.S. Al-Gahtani, Factors affecting threshold chloride for reinforcement corrosion in concrete Cement and Concrete Research. ,vol. 25, pp. 1543- 1555 ,(1995) , 10.1016/0008-8846(95)00148-6
C. Arya, N.R. Buenfeld, J.B. Newman, Factors influencing chloride-binding in concrete Cement and Concrete Research. ,vol. 20, pp. 291- 300 ,(1990) , 10.1016/0008-8846(90)90083-A