Effect of Chromium on the Pitting Resistance of Oil Tube Steel in a Carbon Dioxide Corrosion System
作者： C. F. Chen , M. X. Lu , D. B. Sun , Z. H. Zhang , W. Chang
DOI: 10.5006/1.3278195
关键词: Intergranular corrosion 、 Amorphous solid 、 Corrosion 、 Electrical resistivity and conductivity 、 Pitting corrosion 、 Metallurgy 、 Carbon steel 、 Chromium 、 Carbon dioxide 、 Materials science
摘要: It has been well known that carbon dioxide (CO2) corrosion resulted in the failures of tubing and casing, in which pitting was one of the main failure degradation modes. There are …
allenpress.com
corrosionjournal.org
onepetro.org参考文章(10)
Terje Sontvedt, Gisle Onsrum, Recording of Local Flow Disturbances Behind Obstacles Where Mesa Attack Have Occurred Corrosion. ,(1998)
Madan Gopal, S. Rajappa, Effect of multiphase slug flow on the stability of corrosion product layer Corrosion. ,(1999)
Guenter Schmitt, Gerit Siegmund, Michael Mueller, Christoph Bosch, A Probabilistic Model for Flow Induced Localized Corrosion Corrosion. ,(2000)
Hideki Takabe, Masakatsu Ueda, The Formation Behavior of Corrosion Protective Films of Low Cr Bearing Steels in CO2 Environments Corrosion. ,(2001)
Hideki Takabe, Masakatsu Ueda, Corrosion Resistance of Low Cr Bearing Steel in Sour and Sweet Environments Corrosion. ,(2002)
Zhao Guoxian, Lu Minxu, Bai Zhenquan, Chen Changfeng, Chang Wei, The Ion Passing Selectivity of CO2 Corrosion Scale on N80 Tube Steel Corrosion. ,(2003)
Hideki Takabe, Perry Ian Nice, Masakatsu Ueda, The Development and Implementation of a New Alloyed Steel for Oil and Gas Production Wells Corrosion. ,(2000)
Hitoshi Asahi, Perry Ian Nice, John W. Martin, Koichi Nose, Corrosion Properties of 3% Cr Steels in Oil and Gas Environments Corrosion. ,(2001)
Rolf Nyborg, Arne Dugstad, Mesa Corrosion Attack in Carbon Steel and 0.5% Chromium Steel Corrosion. ,(1998)
J. L. Crolet, N. Thevenot, S. Nesic, Role of Conductive Corrosion Products in the Protectiveness of Corrosion Layers Corrosion. ,vol. 54, pp. 194- 203 ,(1998) , 10.5006/1.3284844