A review of recent developments in Fe3Al-based alloys
作者： C.G. McKamey , J.H. DeVan , P.F. Tortorelli , V.K. Sikka
关键词: Microstructure 、 Weldability 、 Alloy 、 Ultimate tensile strength 、 Corrosion 、 Ternary alloy 、 Embrittlement 、 Metallurgy 、 Structural material 、 Materials science
摘要: … , welds with and without cracks were produced. Successful welds with minimum cracking were produced in an alloy … found to enhance weldability, while zirconium, boron, and TiB2 were …
springer.com
harvard.edu
osti.gov
sci-hub.se 参考文章(90)
J. H. DeVan, H. S. Hsu, M. Howell, Sulfidation/oxidation properties of iron-based alloys containing niobium and aluminum Office of Scientific and Technical Information (OSTI). ,(1989) , 10.2172/5976513
G.J. Yurck, D.A. Shores, Fundamental aspects of high temperature corrosion - II The Electrochemical Society,Pennington, NJ. ,(1986)
P.S. Bishop, J.R. DiStefano, P.F. Tortorelli, Selection of corrosion-resistant materials for use in molten nitrate salts ,(1989)
R. G. Bourdeau, C. M. Adam, M. J. Blackburn, C. V. Law, E. R. Slaughter, Development of Iron Aluminides Defense Technical Information Center. ,(1987) , 10.21236/ADA185190
G C Culbertson, C S Kortovich, Development of Iron Aluminides. ,(1986)
D. R. Holmes, A. Rahmel, Materials and coatings to resist high temperature corrosion Applied Science Publishers. ,(1978)
J.F. Nachman, W.J. Buehler, THERMENOL - A NON STRATEGIC ALUMINUM-IRON BASE ALLOY FOR HIGH TEMPERATURE SERVICE ,(1954)
W.J. Lepkowski, J.W. Holladay, THE PRESENT STATE OF DEVELOPMENT OF IRON-ALUMINUM-BASE ALLOYS ,(1957) , 10.2172/4317904
N.S. Stoloff, C.C. Koch, C.T. Liu, High-temperature ordered intermetallic alloys Materials Research Society,Pittsburgh, PA. ,(1985)
V.K. Sikka, C.G. McKamey, C.R. Howell, R.H. Baldwin, Fabrication and mechanical properties of Fe sub 3 Al-based iron aluminides ,(1990) , 10.2172/6596000