Hygrothermal ageing effect on mechanical properties of FRP laminates
作者： S. Larbi , R. Bensaada , A. Bilek , S. Djebali
DOI: 10.1063/1.4914257
关键词: Materials science 、 Characterization (materials science) 、 Glass fiber 、 Composite material 、 Bending 、 Ageing 、 Epoxy 、 Fibre-reinforced plastic 、 Material Absorption
摘要: The aim of this work is to study the effect hygrothermal aging on mechanical properties two composite materials (carbon fiber / epoxy and glass E vinylester). Two stratifications are studied for each material. Both exposed different environments, sea water deionized at a temperature 40°C. kinetic material absorption plotted. We see an irreversible degradation caused by exposure time. characterization samples in virgin state aged condition achieved with three points bending tests. can significant loss due aging.
scitation.org
harvard.edu
aip.org 
researchgate.net 
sci-hub.se 参考文章(15)
Julien Mercier, Prise en compte du vieillissement et de l'endommagement dans le dimensionnement de structures en matériaux composites École Nationale Supérieure des Mines de Paris. ,(2006)
Józef Stabik, None, Ageing of laminates in boiling NaCl water solution Polymer Testing. ,vol. 24, pp. 101- 103 ,(2005) , 10.1016/J.POLYMERTESTING.2004.06.004
XJ Fan, SW Ricky Lee, Qiang Han, Experimental investigations and model study of moisture behaviors in polymeric materials Microelectronics Reliability. ,vol. 49, pp. 861- 871 ,(2009) , 10.1016/J.MICROREL.2009.03.006
B. Dewimille, A.R. Bunsell, Accelerated ageing of a glass fibre-reinforced epoxy resin in water Composites. ,vol. 14, pp. 35- 40 ,(1983) , 10.1016/0010-4361(83)90141-6
G. Camino, A.Ya. Polishchuk, M.P. Luda, M. Revellino, R. Blancon, J.J. Martinez-Vega, Water ageing of SMC composite materials: a tool for material characterisation Polymer Degradation and Stability. ,vol. 61, pp. 53- 63 ,(1998) , 10.1016/S0141-3910(97)00129-8
R.C. Wyatt, K.H.G. Ashbee, Debonding in carbon fibre/polyester resin composites exposed to water: Comparison with ‘E’ glass fibre composites Fibre Science and Technology. ,vol. 2, pp. 29- 40 ,(1969) , 10.1016/0015-0568(69)90029-3
J.R.M. d'Almeida, Effects of distilled water and saline solution on the interlaminar shear strength of an aramid/epoxy composite Composites. ,vol. 22, pp. 448- 450 ,(1991) , 10.1016/0010-4361(91)90203-S
B.F. Boukhoulda, E. Adda-Bedia, K. Madani, The effect of fiber orientation angle in composite materials on moisture absorption and material degradation after hygrothermal ageing Composite Structures. ,vol. 74, pp. 406- 418 ,(2006) , 10.1016/J.COMPSTRUCT.2005.04.032
A. Kootsookos, A.P. Mouritz, Seawater durability of glass- and carbon-polymer composites Composites Science and Technology. ,vol. 64, pp. 1503- 1511 ,(2004) , 10.1016/J.COMPSCITECH.2003.10.019
Wellington Chu, Lixin Wu, Vistasp M. Karbhari, Durability evaluation of moderate temperature cured E-glass/vinylester systems Composite Structures. ,vol. 66, pp. 367- 376 ,(2004) , 10.1016/J.COMPSTRUCT.2004.04.058