Joining of Cf/SiC composite to Ti alloy using composite filler materials
作者： J. Xiong , J. Huang , Z. Wang , G. Lin , H. Zhang
关键词: Brazing 、 Microstructure 、 Alloy 、 Materials science 、 Shear (sheet metal) 、 Composite material 、 Composite number
摘要: AbstractCf/SiC was successfully joined to Ti alloy with Ag–Cu–Ti–W, Ag–Cu–Ti–SiC and Ag–Cu–Ti–TiC mixed powders by some suitable brazing parameters. Microstructure shear strengths of the preformed joint were investigated. The results showed that W particulate reaction products can uniformly distribute in layer performed joint. These composite layers relaxed thermal stress effectively. characteristics beneficial joint, which had significantly higher than optimal brazed pure Ag–Cu–Ti at room temperature 500°C.
sci-hub.se 参考文章(2)
T. Ishikawa, A Tough, Thermally Conductive Silicon Carbide Composite with High Strength up to 1600°C in Air Science. ,vol. 282, pp. 1295- 1297 ,(1998) , 10.1126/SCIENCE.282.5392.1295
Wendy Hanson, Joining of Ceramics using a Ceramic-modified Braze Alloy Materials Technology. ,vol. 14, pp. 53- 56 ,(1999) , 10.1080/10667857.1999.11752814