Electrochemical Behavior of Three 90Cu-10Ni Tubes from Different Manufacturers After Immersion in 3.5% NaCl Solution
作者： Okpo O. Ekerenam , Aili Ma , Yugui Zheng , Wilfred Emori
DOI: 10.1007/S11665-017-2566-1
关键词: Immersion (virtual reality) 、 Electrochemistry 、 Oxide 、 Polarization (electrochemistry) 、 X-ray photoelectron spectroscopy 、 Surface film 、 Composite material 、 Film resistance 、 Materials science 、 Metallurgy 、 Corrosion
摘要: Investigation on the electrochemical behavior and corrosion product films formed on three 90Cu-10Ni tubes designated as Tubes A, B and C from three different manufacturers with …
harvard.edu
springer.com
sci-hub.se 
researchgate.net 参考文章(42)
Wilhelm Schleich, Application of Copper-Nickel Alloy UNS C70600 for Seawater Service Corrosion. ,(2005)
Kh M Ismail, WA Badawy, Electrochemical and XPS investigations of cobalt in KOH solutions Journal of Applied Electrochemistry. ,vol. 30, pp. 1303- 1311 ,(2000) , 10.1023/A:1026560422090
Y. Kang, G. Zhou, D. Starr, X. Tong, L. Luo, J.C. Yang, Duplex Oxide Formation during Transient Oxidation of Cu-5%Ni(001) Investigated by In situ UHV-TEM and XPS 8th International Symposium on High Temperature Corrosion and Protection of Materials (HTCPM 2012); Les Embiez, France; 20120520 through 20120525. ,(2012)
R. W. Cahn, E. J. Kramer, P. Haasen, Materials science and technology : a comprehensive treatment International Journal of Materials Research. ,vol. 84, pp. 573- 573 ,(1993) , 10.1515/IJMR-1993-840206
Bo Sun, Tianyuan Ye, Qiang Feng, Jinghua Yao, Mumeng Wei, Accelerated Degradation Test and Predictive Failure Analysis of B10 Copper-Nickel Alloy under Marine Environmental Conditions. Materials. ,vol. 8, pp. 6029- 6042 ,(2015) , 10.3390/MA8095290
R.J.K. Wood, S.P. Hutton, D.J. Schiffrin, Mass transfer effects of non-cavitating seawater on the corrosion of Cu and 70Cu-30Ni Corrosion Science. ,vol. 30, pp. 1177- 1201 ,(1990) , 10.1016/0010-938X(90)90198-E
I. Thompson, D. Campbell, Interpreting Nyquist responses from defective coatings on steel substrates Corrosion Science. ,vol. 36, pp. 187- 198 ,(1994) , 10.1016/0010-938X(94)90119-8
M. S. Parvizi, A. Aladjem, J. E. Castle, Behaviour of 90–10 cupronickel in sea water International Materials Reviews. ,vol. 33, pp. 169- 200 ,(1988) , 10.1179/IMR.1988.33.1.169
Khaled M. Ismail, Ahlam M. Fathi, Waheed A. Badawy, The Influence of Ni Content on the Stability of Copper—Nickel Alloys in Alkaline Sulphate Solutions Journal of Applied Electrochemistry. ,vol. 34, pp. 823- 831 ,(2004) , 10.1023/B:JACH.0000035612.66363.A3
J Mathiyarasu, N Palaniswamy, V S Muralidharan, Effect of Nickel Content on the Electrochemical Behaviour of Cupromckel alloy in Neutral Chloride Solutions Portugaliae Electrochimica Acta. ,vol. 17, pp. 45- 56 ,(1999) , 10.4152/PEA.199901045