Oxidation of β-FeAl and Fe-Al alloys

摘要: The oxidation kinetics of the intermetallic phase β-FeAl has been investigated by means thermogravimetry in temperature range 800–1100°C. At temperatures higher than 900°C initially formed metastable aluminium oxides are converted to adherent and slow growing α-Al2O3 scales. rate conversion accelerates with increasing temperature. parabolic constants kp comparable those β-NiAl. The influence Al content on behaviour was exposure experiments at low oxygen partial pressures for samples 5 48 at.% Al. oxide morphology changes only temperature, neither variations nor O2-pressure any influence. In cavities beneath scale metallic matrix. Oxidationsverhalten von und Fe-Al-Legierungen Die Oxidationskinetik der intermetallischen Phase wurde im Temperaturbereich 800–1100°C mittels Thermogravimetrie untersucht. Die anfanglich gebildeten metastabilen Al-Oxide werden oberhalb Oxidationstemperatur eine dichte, nur langsam wachsende α-Al2O3-Schicht umgewandelt. Umwandlungsgeschwindigkeit nimmt mit hoheren Temperaturen zu. Bestimmung parabolischen Zunderkonstanten zeigt gute Ubereinstimmung den kp-Werten fur β-NiAl. Der Einflus Aluminiumkonzentration auf das Oxidationsverhalten Auslagerungsexperimenten an Proben bis bei niedrigen Sauerstoffpartialdrucken Oxidmorphologie hangt ab, nicht aber vom Aluminiumgehalt Sauerstoffpartialdruck. Nur 10 Al-Gehalt α-Fe(Al)-Phase tritt innere Oxidation auf, oder Al-reichen bildet sich schutzende, asere Al2O3-Schicht. Bei Al-Gehalten bilden metallischen Matrix unterhalb Oxidschicht Hohlraume aus.