Effect of 0.1% vanadium addition on precipitation behavior and mechanical properties of Al-6063 commercial alloy
作者： S. Camero , E. S. Puchi , G. Gonzalez , None
DOI: 10.1007/S10853-006-0794-0
关键词: Vanadium 、 Alloy 、 Materials science 、 Precipitation (chemistry) 、 Microstructure 、 Casting 、 Metallurgy 、 Ingot 、 Precipitation kinetics
摘要: The effect of 0.1 wt% vanadium additions on the precipitation behavior and mechanical properties a commercial Al-6063 alloy were studied. A master containing 3 V was added during casting. cast ingot homogenized, extruded cooled employing two different cooling modes: forced air water. Further aging carried out following standard T5 T6 treatments for alloys with without vanadium. microstructural characterization, properties, fractografic study out. addition 0.1% to under treatment, accelerates kinetics β″ β′ phases. show similar behavior, co-existence is observed in both alloys. In general, Al 6063 have detrimental showing only beneficial certain specific conditions.
springer.com
harvard.edu
sci-hub.se 参考文章(21)
S.P. Ringer, K. Hono, Microstructural Evolution and Age Hardening in Aluminium Alloys: Atom Probe Field-Ion Microscopy and Transmission Electron Microscopy Studies Materials Characterization. ,vol. 44, pp. 101- 131 ,(2000) , 10.1016/S1044-5803(99)00051-0
H. Tanihata, T. Sugawara, K. Matsuda, S. Ikeno, Effect of casting and homogenizing treatment conditions on the formation of Al–Fe–Si intermetallic compounds in 6063 Al–Mg–Si alloys Journal of Materials Science. ,vol. 34, pp. 1205- 1210 ,(1999) , 10.1023/A:1004504805781
K. Matsuda, Y. Sakaguchi, Y. Miyata, Y. Uetani, T. Sato, A. Kamio, S. Ikeno, Precipitation sequence of various kinds of metastable phases in Al-1.0mass% Mg2Si-0.4mass% Si alloy Journal of Materials Science. ,vol. 35, pp. 179- 189 ,(2000) , 10.1023/A:1004769305736
L. F. Mondolfo, Aluminum Alloys: Structure and Properties ,(1976)
Yasuya Ohmori, Long Chau Doan, Yoshitsugu Matsuura, Sengo Kobayashi, Kiyomichi Nakai, Morphology and Crystallography of β-Mg2Si Precipitation in Al-Mg-Si Alloys Materials Transactions. ,vol. 42, pp. 2576- 2583 ,(2001) , 10.2320/MATERTRANS.42.2576
M Takeda, F Ohkubo, T Shirai, M Takeda, Stability of metastable phases and microstructures in the ageing process of Al–Mg–Si ternary alloys Journal of Materials Science. ,vol. 33, pp. 2385- 2390 ,(1998) , 10.1023/A:1004355824857
P. Schwellinger, Reply to discussion of “mechanism of ductile intergranular fracture” Scripta Metallurgica. ,vol. 13, pp. 497- 498 ,(1979) , 10.1016/0036-9748(79)90076-0
P. Schwellinger, On the fracture mechanisms in AlMgSi-alloys Scripta Metallurgica. ,vol. 14, pp. 769- 772 ,(1980) , 10.1016/0036-9748(80)90286-0
J. C. Blade, A. J. Bryant, A. T. Thomas, Alloy composition and microstructure control in relation to mechanical working for aluminium alloys Metals technology. ,vol. 3, pp. 380- 386 ,(1976) , 10.1179/030716976803391584
Kenji Matsuda, Tsutomu Naoi, Kaname Fujii, Yasuhiro Uetani, Tatsuo Sato, Akihiko Kamio, Susumu Ikeno, Crystal structure of the β′′ phase in an Al–l.0mass%Mg2Si–0.4mass%Si alloy Materials Science and Engineering: A. ,vol. 262, pp. 232- 237 ,(1999) , 10.1016/S0921-5093(98)00962-9