Fatigue crack propagation in friction stir welded and parent AA6082
作者： Mats Ericsson , Rolf Sandström
关键词: Residual stress 、 Fracture mechanics 、 Crack closure 、 Metallurgy 、 Materials science 、 Fatigue crack propagation 、 Friction stir welding 、 Friction welding 、 Alloy 、 Welding
摘要: The fatigue crack propagation characteristics of a friction stir welded AI-Mg-Si alloy, 6082, have been investigated. electrical potential drop method was used for measurements. A low and hig ...
sci-hub.se 参考文章(9)
T. Ghidini, C. Dalle Donne, G. Biallas, G. Raimbeaux, Effects of Weld Imperfections and Residual Stresses on the Fatigue Crack Propagation in Friction Stir Welded Joints ,(2000)
K Walker, The Effect of Stress Ratio During Crack Propagation and Fatigue for 2024-T3 and 7075-T6 Aluminum ASTM International. ,(1970) , 10.1520/STP32032S
W. Elber, The Significance of Fatigue Crack Closure ASTM Spec Tech Publ (Am Soc Test Mater). ,vol. 486, pp. 230- 242 ,(1971) , 10.1520/STP26680S
M Ericsson, Influence of welding speed on the fatigue of friction stir welds, and comparison with MIG and TIG International Journal of Fatigue. ,vol. 25, pp. 1379- 1387 ,(2003) , 10.1016/S0142-1123(03)00059-8
P PARIS, Service load fatigue damage ? a historical perspective International Journal of Fatigue. ,vol. 21, pp. 35- 46 ,(1999) , 10.1016/S0142-1123(99)00054-7
D Kujawski, A new (ΔK+Kmax)0.5 driving force parameter for crack growth in aluminum alloys International Journal of Fatigue. ,vol. 23, pp. 733- 740 ,(2001) , 10.1016/S0142-1123(01)00023-8
K DONALD, An evaluation of $Delta;Keff estimation procedures on 6061-T6 and 2024-T3 aluminum alloys*1 International Journal of Fatigue. ,vol. 21, pp. 47- 57 ,(1999) , 10.1016/S0142-1123(99)00055-9
P.S Pao, S.J Gill, C.R Feng, K.K Sankaran, Corrosion-fatigue crack growth in friction stir welded Al 7050 Scripta Materialia. ,vol. 45, pp. 605- 612 ,(2001) , 10.1016/S1359-6462(01)01070-3
R. G. Forman, V. E. Kearney, R. M. Engle, Numerical Analysis of Crack Propagation in Cyclic-Loaded Structures Journal of Basic Engineering. ,vol. 89, pp. 459- 463 ,(1967) , 10.1115/1.3609637