FeAl–TiN nanocomposite produced by reactive ball milling and hot-pressing consolidation
作者： Marek Krasnowski , Tadeusz Kulik
DOI: 10.1016/S1359-6462(03)00112-X
关键词: Materials science 、 Metallurgy 、 Powder mixture 、 Consolidation (soil) 、 Nitrogen 、 Ball mill 、 FEAL 、 Hot pressing 、 Nanocomposite 、 Tin
摘要: Abstract The FeAl–TiN nanocomposite was produced by milling an elemental powder mixture of Al–Fe–Ti in nitrogen, followed hot-pressing consolidation under 8 GPa pressure. average hardness the nanocomposites consolidated at temperatures 750 and 950 °C are 1424 HV 0.2 1461 respectively, density is 97% theoretical value both cases.
elsevier.com
sci-hub.se 参考文章(4)
M Krasnowski, A Witek, T Kulik, The FeAl–30%TiC nanocomposite produced by mechanical alloying and hot-pressing consolidation Intermetallics. ,vol. 10, pp. 371- 376 ,(2002) , 10.1016/S0966-9795(02)00009-2
R.M. Imayev, N.K. Gabdullin, G.A. Salishchev, O.N. Senkov, V.M. Imayev, F.H. Froes, Effect of grain size and partial disordering on ductility of Ti3Al in the temperature range of 20–600°C Acta Materialia. ,vol. 47, pp. 1809- 1821 ,(1999) , 10.1016/S1359-6454(99)00044-0
F. H. Froes, C. Suryanarayana, D. Eliezer, Synthesis, properties and applications of titanium aluminides Journal of Materials Science. ,vol. 27, pp. 5113- 5140 ,(1992) , 10.1007/BF02403806
M. Angiolini, Marek Krasnowski, G. Mazzone, Amelia Montone, M. Urchulutegui, Marco Vittori Antisari, Electron Microscopy Characterization of Cu-Fe and Ag-Fe Alloys Obtained by Plastic Deformation Materials Science Forum. ,vol. 195, pp. 13- 18 ,(1995) , 10.4028/WWW.SCIENTIFIC.NET/MSF.195.13