Enhanced ballistic performance of polymer fibers
作者： Brian D. Arvidson , Ashok Bhatnagar , Lori L. Wagner , Chok Bin C. Tan
DOI:
关键词: Composite material 、 Protein filament 、 Fiber 、 Fiber diameter 、 Area density 、 Polymer 、 Fiber Chemistry 、 Modulus 、 Materials science
摘要: Ballistic resistant materials having improved strength and lighter weights. More particularly, ballistic fabrics produced from drawn, high modulus fibers a reduced fiber diameter physical properties, without changing other properties such as chemistry, binder resin type content. The incorporate low denier per filament monofilament fibers, multifilament or combination of in specialized fabric construction to form fine layers enhanced areal density altering the weight, weight corresponding reduction performance.
google.co.uk 参考文章(61)
Andrew D. Park, Ballistic resistant composite for hard-armor application ,(1995)
Kenji Iizuka, Shigeo Abiru, Bulletproof fabric and process for its production ,(1997)
Rene Christian Van Der Burg, Leonardus Lambertus Henricus Van Der Loo, Non-woven layer consisting substantially of short polyolefin fibers ,(1993)
Brian D. Arvidson, Chok B. Tan, Thomas Y-T. Tam, Process for making uniform high strength yarns and fibrous sheets ,(2007)
David Verlin Cunningham, Unique ballistic composition ,(2004)
Ashok Bhatnagar, Brian Duane Arvidson, Impact resistant rigid composite and method of manufacture ,(2001)
Charles R. Arnett, Qiang Zhou, John A. Young, John E. Hermes, Thomas Yiu-Tai Tam, Process for the preparation of UHMW multi-filament poly(alpha-olefin) yarns ,(2007)
Paul Smith, Pieter J. Lemstra, Process for the preparation of filaments of high tensile strength and modulus ,(1980)
Jacques P. L. Pijpers, Paul Smith, Robert Kirschbaum, Pieter J. Lemstra, Process for the production of polymer filaments having high tensile strength ,(1982)
Lien-Tai Chen, Dah-Ming Lee, Ming-Tao Yeh, Wei-Liang Chen, Process for producing high tenacity and high modulus polyethylene fibers ,(1993)