A comparison of the scaling behaviour of pure iron-chromium and nickel-chromium alloys in oxygen
作者： G.C. Wood , T. Hodgkiess , D.P. Whittle
DOI: 10.1016/S0010-938X(66)80004-5
关键词: Alloy 、 Spinel 、 Metallurgy 、 Scaling 、 Oxygen 、 Metal 、 Materials science 、 Corrosion 、 Cracking 、 Chromium
摘要: … for chromium-rich alloys because metallic interdiffusion is slower and oxygen solubility in the alloy is apparently greater for fcc Ni-Cr alloys than for bcc Fe-Cr alloys. With more dilute …
elsevier.com
sci-hub.se 参考文章(6)
H. J. Yearian, J. M. Kortright, R. H. Langenheim, Lattice Parameters of the FeFe(2—x)CrxO4Spinel System The Journal of Chemical Physics. ,vol. 22, pp. 1196- 1198 ,(1954) , 10.1063/1.1740331
G.C. Wood, D.P. Whittle, The unusual scaling behaviour of iron-22·9% chromium in air at 1100°C☆ Corrosion Science. ,vol. 4, pp. 293- 313 ,(1964) , 10.1016/0010-938X(64)90027-7
G.C. Wood, D.P. Whittle, On the mechanism of oxidation of iron-16·4% chromium at high temperature☆ Corrosion Science. ,vol. 4, pp. 263- 292 ,(1964) , 10.1016/0010-938X(64)90026-5
C. A. Phalnikar, E. B. Evans, W. M. Baldwin, High Temperature Scaling of Cobalt‐Chromium Alloys Journal of The Electrochemical Society. ,vol. 103, pp. 429- 438 ,(1956) , 10.1149/1.2430374
G.C. Wood, T.G. Wright, The scaling of nickel and nickel-cobalt alloys in air Corrosion Science. ,vol. 5, pp. 841- 857 ,(1965) , 10.1016/S0010-938X(65)80013-0
D. LAI, R. J. BORG, M. J. BRABERS, J. D. MACKENZIE, C. E. BIRCHENALL, Oxidation of Iron-Chromium Alloys at 750–1025C Corrosion. ,vol. 17, ,(1961) , 10.5006/0010-9312-17.7.109