A contribution to the semicontinuous emulsion polymerization. II. Copolymerization of butyl methacrylate and butyl acrylate

作者: Jaromír Šňpárek

DOI: 10.1002/APMC.1972.050250111

关键词: Butyl methacrylatePolymerizationCopolymerMonomerEmulsion polymerizationReactivity (chemistry)Butyl acrylateChemistrySteady state (chemistry)Polymer chemistry

摘要: A semicontinuous emulsion copolymerization of butyl methacrylate and acrylate was investigated. Under the conditions used, polymerization rate determined by feeding monomers. At a steady state, when ratio free monomers in reactor remained constant, reactivity ratios r1 = 2.21 r2 0.27 were found. These compared with those calculated from published Q-e values. Die semikontinuierliche Emulsionspolymerisation von Butylmethacrylat und Butylacrylat wurde untersucht. Die Polymerisationsgeschwindigkeit durch die Zulaufgeschwindigkeit bestimmt. Fur den stationaren Zustand, bei dem das Monomerenverhaltnis konstant blieb, wurden Copolymerisationsparameter 2,21 0,27 gefunden. Diese Werte mit aus veroffentlichten Q- e-Werten berechneten Parametern verglichen.

参考文章(0)