Glaze composition and antifouling ceramic ware
作者： Kanjanatanom Othong , Kazuhiro Matsuura , Shigeru Ishiki , Masayuki Ishihara
DOI:
关键词:
摘要: A glaze composition can be used to provide a layer having excellent antifouling performance and visual beauty. The contains forming material, which has determined such that baked product obtained by baking the comprises 55.0 67.0 wt% of SiO2; 8.0 11.0 Al2O3; 2.0 SnO2; 15.0 21.0 divalent metal oxide; 4.0 6.0 monovalent oxide, with respect total weight product. When is formed use this composition, it resists contamination. Even when dirt deposits on layer, easily removed from layer. In addition, beautiful semi-opaque luster reduction in pore generation amount.
google.st 参考文章(9)
Stuart W. Ries, Elie E. Saad, Rare earth-containing alkali silicate frits and their use for the preparation of porcelain enamel coatings with improved cleanability ,(1993)
Marzia Barattini, Paolo Bertocchi, Emanuela Neri, Bruno Burzacchini, Ceramic tile and glaze for use thereon ,(1997)
Makoto Hayakawa, Tomoyasu Ichiki, Koichi Hayashi, Katsuhiro Kawakami, Hirotaka Ishibashi, Atsushi Kitamura, Toshihiro Aoshima, Mitsuyoshi Machida, Masaaki Ito, Satoshi Horiuchi, Masami Ando, Sanitary ware and process for producing the same ,(1999)
Alain Aronica, Thierry Souchard, Catalytic porcelain enamel coating composition ,(1998)
Josef Francel, Daniel R. Stewart, Uriah Horn, Lead-free and cadmium-free glass frit compositions for glazing, enameling and decorating ,(1984)
Robert L. Hyde, Porcelain enamel composition and substrates coated therewith ,(1986)
Peter Thometzek, Heinrich Christ, Granular materials, a process for their production and their use ,(1993)
Eugene F. O'Conor, Leadless glazes for whiteware ,(1981)
Morimoto Shigeki, Sugiura Kenji, COMPOSITION FOR POROUS GLASS ,(1991)