In situ observation of dynamic recrystallization in five-nine aluminum by a transmission Laue method
作者： Hiroshi Yamagata
DOI: 10.1016/0956-716X(94)90595-9
关键词:
摘要: Abstract An in situ observation of X-ray diffraction patterns a five-nine aluminum single crystal was performed during 533 K compression test where regular multipeak stress oscillation generated. Asterism patterns, characteristic strained crystals, were observed the work hardening stages. Spot coarse grain structures containing fewer substructures, appeared softening These observations prove that is caused by dynamic recrystallization.
osti.gov
sci-hub.se 参考文章(5)
H.J. McQueen, W. Blum, S. Straub, M.E. Kassner, Dynamic grain growth a restoration mechanism in 99.999 Al Scripta Metallurgica et Materialia. ,vol. 28, pp. 1299- 1304 ,(1993) , 10.1016/0956-716X(93)90472-5
Bernard Dennis Cullity, Elements of X-ray diffraction ,(1956)
H. Yamagata, Multipeak stress oscillations of five-nine-purity aluminum during a hot compression test Scripta Metallurgica Et Materialia. ,vol. 27, pp. 201- 203 ,(1992) , 10.1016/0956-716X(92)90113-S
H. Yamagata, Yamaha Motor Co., Ltd., Microstructural evolution of single-crystalline aluminum during multipeak stress oscillation at 623 K Scripta Metallurgica et Materialia. ,vol. 27, pp. 1157- 1160 ,(1992) , 10.1016/0956-716X(92)90591-2
H Yamagata, Dynamic recrystallization of single-crystalline aluminum during compression tests Scripta Metallurgica Et Materialia. ,vol. 27, pp. 727- 732 ,(1992) , 10.1016/0956-716X(92)90496-2