Passivity breakdown, its relation to pitting and stress-corrosion-cracking processes
作者： J.R. Galvele , R.M. Torresi , R.M. Carranza
DOI: 10.1016/0010-938X(90)90163-Y
关键词:
摘要: Repassivation kinetics of metals has been frequently related to the susceptibility to localized types of corrosion such as pitting, crevice corrosion and stress corrosion cracking (SCC). …
elsevier.com
sci-hub.se 参考文章(12)
K. N. Tu, Treatise on Materials Science and Technology ,(1979)
I. Gardiazabal, R. Córdova, H. Gómez, R. Schrebler, The electrochemical behaviour of zircaloy-4 electrodes in acid iodide solution Journal of Electroanalytical Chemistry and Interfacial Electrochemistry. ,vol. 240, pp. 299- 308 ,(1988) , 10.1016/0022-0728(88)80330-9
N. Sato, A theory for breakdown of anodic oxide films on metals Electrochimica Acta. ,vol. 16, pp. 1683- 1692 ,(1971) , 10.1016/0013-4686(71)85079-X
R.M Carranza, J.R Galvele, Repassivation kinetics in stress corrosion cracking—I. Type AISI 304 stainless steel in chloride solutions Corrosion Science. ,vol. 28, pp. 233- 249 ,(1988) , 10.1016/0010-938X(88)90107-2
JoséR. Galvele, A stress corrosion cracking mechanism based on surface mobility Corrosion Science. ,vol. 27, pp. 1- 33 ,(1987) , 10.1016/0010-938X(87)90117-X
R.M Carranza, J.R Galvele, Repassivation kinetics in stress corrosion cracking — II. α-Brass in non-ammoniacal solutions Corrosion Science. ,vol. 28, pp. 851- 865 ,(1988) , 10.1016/0010-938X(88)90034-0
JoséR. Galvele, Transport processes in passivity breakdown—II. Full hydrolysis of the metal ions Corrosion Science. ,vol. 21, pp. 551- 579 ,(1981) , 10.1016/0010-938X(81)90009-3
R.B. Rebak, R.M. Carranza, J.R. Galvele, The stress corrosion cracking mechanism of α-brass in NaNO2 solutions Corrosion Science. ,vol. 28, pp. 1089- 1106 ,(1988) , 10.1016/0010-938X(88)90103-5
Jose R. Galvele, Transport Processes and the Mechanism of Pitting of Metals Journal of The Electrochemical Society. ,vol. 123, pp. 464- 474 ,(1976) , 10.1149/1.2132857
JOHN R. AMBROSE, 4 - Repassivation Kinetics Treatise on Materials Science and Technology. ,vol. 23, ,(1983) , 10.1016/B978-0-12-633670-2.50009-7