Phosphate-bonded calcium aluminate cements
作者： Toshifumi Sugama
DOI:
关键词:
摘要: A method is described for making a rapid-setting phosphate-bonded cementitious material. powdered aluminous cement mixed with an aqueous solution of ammonium phosphate. The mixture allowed to set form amorphous material which also may be hydrothermally treated at temperature from about 120° C. 300° crystal-containing Also are the products this and composition includes polyphosphate.
osti.gov
google.co.jp 参考文章(15)
Torben Christen Hansen, Thomas Ringsholt, Structural building components and method for production on the basis of laterite ,(1975)
Greene Wallace Strother, Walter Warren Henslee, Phosphate bonding of reactive spinels for use as refractory materials ,(1983)
Toshifumi Sugama, Lawrence E. Kukacka, Magnesium phosphate glass cements with ceramic-type properties ,(1982)
Yoshiharu Watanabe, Koji Nakagawa, Concrete composition for making concrete moldings and method for making such concrete moldings ,(1979)
Oshio Akira, Eto Kiyomitsu, Nishi Seiya, Method of producing high strength mortar or concrete ,(1970)
Sota Nakano, Masaaki Ozawa, Process for production of cellular concrete ,(1985)
Takeru Murakami, Kouichi Tateno, Kazuto Ichimaru, Tomisaburo Azuma, Process of producing calcium aluminate monosulfate hydrate ,(1975)
Etsuo Sakai, Yasuhito Fushii, Tutomu Kida, Yukio Sasagawa, Hydraulic material composition having high strength ,(1987)
Toshifumi Sugama, Neal R. Carciello, Strength Development in Phosphate‐Bonded Calcium Aluminate Cements Journal of the American Ceramic Society. ,vol. 74, pp. 1023- 1030 ,(1991) , 10.1111/J.1151-2916.1991.TB04338.X
Takeo Hattori, Yasuhiko Lwadate, Hydrothermal Preparation of Calcium Hydroxyapatite Powders Journal of the American Ceramic Society. ,vol. 73, pp. 1803- 1805 ,(1990) , 10.1111/J.1151-2916.1990.TB09841.X