Flow Behavior and Microstructural Evolution of a 7039 Aluminum Alloy during Hot Deformation
作者： Hui Zhong Li , Xiao Peng Liang , Min Song , Min Zeng
DOI: 10.4028/WWW.SCIENTIFIC.NET/AMR.239-242.2395
关键词:
摘要: The flow behavior of a 7039 aluminum alloy and the corresponding microstructural evolution during hot deformation were studied by Gleeble-1500 thermal simulation tests, EBSD TEM observations with temperatures ranging from 300 °C to 500 under strain rates 0.01 s-1 10 s-1. It has been shown that stress increases decrease in temperature increase rate. degree dynamic recrystallization (DRX) rate alloy. complete occurs at
sci-hub.se 参考文章(13)
Huizhong Li, Zhou Li, Min Song, Xiaopeng Liang, Feifei Guo, Hot deformation behavior and microstructural evolution of Ag-containing 2519 aluminum alloy Materials & Design. ,vol. 31, pp. 2171- 2176 ,(2010) , 10.1016/J.MATDES.2009.10.061
H. Yamagata, Dynamic recrystallization and dynamic recovery in pure aluminum at 583K Acta Metallurgica Et Materialia. ,vol. 43, pp. 723- 729 ,(1995) , 10.1016/0956-7151(94)00267-L
H.E. Hu, L. Zhen, L. Yang, W.Z. Shao, B.Y. Zhang, Deformation behavior and microstructure evolution of 7050 aluminum alloy during high temperature deformation Materials Science and Engineering: A. ,vol. 488, pp. 64- 71 ,(2008) , 10.1016/J.MSEA.2007.10.051
Hui Zhang, Luoxing Li, Deng Yuan, Dashu Peng, Hot deformation behavior of the new Al–Mg–Si–Cu aluminum alloy during compression at elevated temperatures Materials Characterization. ,vol. 58, pp. 168- 173 ,(2007) , 10.1016/J.MATCHAR.2006.04.012
Chang Gil Lee, Sunghak Lee, Correlation of Dynamic Torsional Properties with Adiabatic Shear Banding Behavior in Ballistically Impacted Aluminum- Lithium Alloys Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 29, pp. 227- 235 ,(1998) , 10.1007/S11661-998-0175-1
William H. Van Geertruyden, Wojciech Z. Misiolek, Paul T. Wang, Grain structure evolution in a 6061 aluminum alloy during hot torsion Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 419, pp. 105- 114 ,(2006) , 10.1016/J.MSEA.2005.12.018
Baolute Ren, James G. Morris, Microstructure and texture evolution of Al during hot and cold rolling Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 26, pp. 31- 40 ,(1995) , 10.1007/BF02669792
H.J. McQueen, E. Fry, J. Belling, Comparative constitutive constants for hot working of Al-4.4Mg-0.7Mn (AA5083) Journal of Materials Engineering and Performance. ,vol. 10, pp. 164- 172 ,(2001) , 10.1361/105994901770345178
H. Yamagata, Y. Ohuchida, N. Saito, M. Otsuka, Nucleation of new grains during discontinuous dynamic recrystallization of 99.998 mass% Aluminum at 453 K Scripta Materialia. ,vol. 45, pp. 1055- 1061 ,(2001) , 10.1016/S1359-6462(01)01139-3
H.J. McQueen, S. Yue, N.D. Ryan, E. Fry, Hot working characteristics of steels in austenitic state Journal of Materials Processing Technology. ,vol. 53, pp. 293- 310 ,(1995) , 10.1016/0924-0136(95)01987-P