Controlling factors and mechanisms of fatigue crack growth influenced by high pressure of gaseous hydrogen in a commercially pure iron
作者： Tomoki Shinko , Damien Halm , Guillaume Benoit , Gilbert Hénaff
DOI: 10.1016/J.TAFMEC.2020.102885
关键词:
摘要: … It has been established for quite a long while now that Hydrogen Embrittlement (HE) decreases the durability of many structures exposed to environments which can act as a source of …
sci-hub.st 参考文章(85)
Y. Murakami, R.O. Ritchie, Effects of hydrogen on fatigue-crack propagation in steels Gaseous Hydrogen Embrittlement of Materials in Energy Technologies#R##N#The Problem, its Characterisation and Effects on Particular Alloy Classes. pp. 379- 417 ,(2012) , 10.1533/9780857093899.2.379
Noriko TSUTSUMI, Yukitaka MURAKAMI, Saburo MATSUOKA, 炭素量0.08mass%の配管用炭素鋼鋼管の疲労き裂進展とストレッチゾーンに及ぼす水素の影響 Transactions of the Japan Society of Mechanical Engineers. A. ,vol. 74, pp. 1528- 1537 ,(2008) , 10.1299/KIKAIA.74.1528
Henry J. Cialone, John H. Holbrook, Sensitivity of Steels to Degradation in Gaseous Hydrogen ASTM International. ,(1988) , 10.1520/STP45297S
M.B. Djukic, V. Sijacki Zeravcic, G.M. Bakic, A. Sedmak, B. Rajicic, Hydrogen damage of steels: A case study and hydrogen embrittlement model Engineering Failure Analysis. ,vol. 58, pp. 485- 498 ,(2015) , 10.1016/J.ENGFAILANAL.2015.05.017
M. Nagumo, Function of Hydrogen in Embrittlement of High-strength Steels Isij International. ,vol. 41, pp. 590- 598 ,(2001) , 10.2355/ISIJINTERNATIONAL.41.590
A. Alvaro, I. Thue Jensen, N. Kheradmand, O.M. Løvvik, V. Olden, Hydrogen embrittlement in nickel, visited by first principles modeling, cohesive zone simulation and nanomechanical testing International Journal of Hydrogen Energy. ,vol. 40, pp. 16892- 16900 ,(2015) , 10.1016/J.IJHYDENE.2015.06.069
Ryosuke Matsumoto, Honami Imanishi, Shinya Taketomi, Dislocation dynamics analysis of hydrogen embrittlement in alpha iron based on atomistic investigations ICF13. ,(2013)
John Crank, The mathematics of diffusion ,(1956)
E. S. Drexler, A. J. Slifka, R. L. Amaro, N. Barbosa, D. S. Lauria, L. E. Hayden, D. G. Stalheim, Fatigue crack growth rates of API X70 pipeline steel in a pressurized hydrogen gas environment Fatigue & Fracture of Engineering Materials & Structures. ,vol. 37, pp. 517- 525 ,(2014) , 10.1111/FFE.12133
R. A. Oriani, A mechanistic theory of hydrogen embrittlement of steels Berichte der Bunsengesellschaft für physikalische Chemie. ,vol. 76, pp. 848- 857 ,(1972) , 10.1002/BBPC.19720760864