Safe life and damage tolerance aspects of railway axles – A review

作者: U. Zerbst , S. Beretta , G. Köhler , A. Lawton , M. Vormwald

DOI: 10.1016/J.ENGFRACMECH.2012.09.029

关键词:

摘要: … tolerance methods applied to railway axles. It describes failure … reduce the fatigue strength of axles during service. Potential … 4b to a hollow driving axle of a high speed train with tilting …

参考文章(135)
V. Linhart, I. Černý, An effect of strength of railway axle steels on fatigue resistance under press fit Engineering Fracture Mechanics. ,vol. 78, pp. 731- 741 ,(2011) , 10.1016/J.ENGFRACMECH.2010.11.023
M. Madia, S. Beretta, M. Schödel, U. Zerbst, M. Luke, I. Varfolomeev, Stress intensity factor solutions for cracks in railway axles Engineering Fracture Mechanics. ,vol. 78, pp. 764- 792 ,(2011) , 10.1016/J.ENGFRACMECH.2010.03.019
S. Beretta, M. Carboni, Experiments and stochastic model for propagation lifetime of railway axles Engineering Fracture Mechanics. ,vol. 73, pp. 2627- 2641 ,(2006) , 10.1016/J.ENGFRACMECH.2006.04.024
A. WORMSEN, B. SJÖDIN, G. HÄRKEGÅRD, A. FJELDSTAD, Non‐local stress approach for fatigue assessment based on weakest‐link theory and statistics of extremes Fatigue & Fracture of Engineering Materials & Structures. ,vol. 30, pp. 1214- 1227 ,(2007) , 10.1111/J.1460-2695.2007.01190.X
A LANCIOTTI, L LAZZERI, Effects of spectrum variations on fatigue crack growth International Journal of Fatigue. ,vol. 14, pp. 319- 324 ,(1992) , 10.1016/0142-1123(92)90483-S
K SHIOZAWA, Y MORII, S NISHINO, L LU, Subsurface crack initiation and propagation mechanism in high-strength steel in a very high cycle fatigue regime International Journal of Fatigue. ,vol. 28, pp. 1521- 1532 ,(2006) , 10.1016/J.IJFATIGUE.2005.08.015
Dolley, Lee, Wei, The effect of pitting corrosion on fatigue life Fatigue & Fracture of Engineering Materials & Structures. ,vol. 23, pp. 555- 560 ,(2000) , 10.1046/J.1460-2695.2000.00323.X