Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag — Part I: Effect of MgO
作者： M. Ben Haha , B. Lothenbach , G. Le Saout , F. Winnefeld
DOI: 10.1016/J.CEMCONRES.2011.05.002
关键词:
摘要: … mainly at bridging sites [22], [23], does not influence the molar volume of the tobermorite-like C–S–H, as the incorporation of Al has been reported to stabilise the 14-Å tobermorite [24]. …
osti.gov
elsevier.com
sci-hub.se 参考文章(62)
U Berner, E Curti, D Kulik, MODELLING CHEMICAL EQUILIBRIUM PARTITIONING WITH THE GEMS-PSI CODE ,(2004)
A. Fernández-Jiménez, J.G. Palomo, F. Puertas, Alkali-activated slag mortars Cement and Concrete Research. ,vol. 29, pp. 1313- 1321 ,(1999) , 10.1016/S0008-8846(99)00154-4
Philippe Pochet, A Quantitative Analysis P.I.E.-Peter Lang. pp. 89- 117 ,(2006)
A.R Brough, A Atkinson, Sodium silicate-based, alkali-activated slag mortars: Part I. Strength, hydration and microstructure Cement and Concrete Research. ,vol. 32, pp. 865- 879 ,(2002) , 10.1016/S0008-8846(02)00717-2
B. Lothenbach, A. Gruskovnjak, Hydration of alkali-activated slag: thermodynamic modelling Advances in Cement Research. ,vol. 19, pp. 81- 92 ,(2007) , 10.1680/ADCR.2007.19.2.81
Aaron R. Sakulich, Edward Anderson, Caroline L. Schauer, Michel W. Barsoum, Influence of Si:Al ratio on the microstructural and mechanical properties of a fine-limestone aggregate alkali-activated slag concrete Materials and Structures. ,vol. 43, pp. 1025- 1035 ,(2010) , 10.1617/S11527-009-9563-2
Karen L. Scrivener, Shao-Dong Wang, Hydration products of alkali activated slag cement Cement and Concrete Research. ,vol. 25, pp. 561- 571 ,(1995) , 10.1016/0008-8846(95)00045-E
R.K Iler, Effect of adsorbed alumina on the solubility of amorphous silica in water Journal of Colloid and Interface Science. ,vol. 43, pp. 399- 408 ,(1973) , 10.1016/0021-9797(73)90386-X
Eric H. Oelkers, General kinetic description of multioxide silicate mineral and glass dissolution Geochimica et Cosmochimica Acta. ,vol. 65, pp. 3703- 3719 ,(2001) , 10.1016/S0016-7037(01)00710-4
I.G. Richardson, Tobermorite/jennite- and tobermorite/calcium hydroxide-based models for the structure of C-S-H: applicability to hardened pastes of tricalcium silicate, β-dicalcium silicate, Portland cement, and blends of Portland cement with blast-furnace slag, metakaolin, or silica fume Cement and Concrete Research. ,vol. 34, pp. 1733- 1777 ,(2004) , 10.1016/J.CEMCONRES.2004.05.034