How proper similitude can improve our understanding of crack closure and plasticity in fatigue
DOI: 10.1016/J.IJFATIGUE.2015.04.011
关键词:
摘要: … plasticity induced crack closure, as first observed by Elber [33], [34]. Occasionally other closure mechanisms are considered, but plasticity … do not exhibit significant plasticity. Fatigue in …
core.ac.uk
tudelft.nl
elsevier.com参考文章(66)
P.C. Paris, D.O. Harris, Engineering Evaluation of the Status of Utilization of Beryllium From the Viewpoint of Fracture Mechanics. Other Information: From Beryllium Conference, Arlington, Va. UNCL. Orig. Receipt Date: 31-DEC-70. ,(1970) , 10.2172/4134787
Walter Illg, Arthur J Mcevily, The rate of fatigue-crack propagation in two aluminum alloys ,(1958)
AU de Koning, A Simple Crack Closure Model for Prediction of Fatigue Crack Growth Rates Under Variable-Amplitude Loading ASTM special technical publications. pp. 63- 85 ,(1981) , 10.1520/STP28791S
D. Taylor, A compendium of fatigue thresholds and growth rates EMAS. ,(1985)
Jaap Schijve, Fatigue of structures and materials ,(2001)
Royce G. Forman, Sambi R. Mettu, Behavior of surface and corner cracks subjected to tensile and bending loads in a Ti-6Al-4V alloy ,(1992)
J Schijve, Fatigue Crack Closure: Observations and Technical Significance Delft University of Technology, Department of Aerospace Engineering, Report LR-485. ,(1986) , 10.1520/STP27198S
Paris, FRACTURE MECHANICS AND FATIGUE: A HISTORICAL PERSPECTIVE Fatigue & Fracture of Engineering Materials & Structures. ,vol. 21, pp. 535- 540 ,(2008) , 10.1046/J.1460-2695.1998.00054.X
N.E. Frost, The Growth of Fatigue Cracks ICF1, Japan 1965. ,(2012)
C.Michael Hudson, Joseph T. Scardina, Effect of stress ratio on fatigue-crack growth in 7075-T6 aluminum-alloy sheet Engineering Fracture Mechanics. ,vol. 1, pp. 429- 446 ,(1969) , 10.1016/0013-7944(69)90003-4