A study of the stresses generated in zirconia films during the oxidation of zirconium alloys
作者： C. Roy , B. Burgess
DOI: 10.1007/BF00614620
关键词:
摘要: … While the onset of creep in the base metal during oxidation was reliably detected in the bending rate curves, there was no clear discontinuity in the extension rate curves which could be …
springer.com
osti.gov
sci-hub.se 参考文章(8)
B. Griggs, H. P. Maffei, D. W. Shannon, Multiple Rate Transitions in the Aqueous Corrosion of Zircaloy Journal of The Electrochemical Society. ,vol. 109, pp. 665- 668 ,(1962) , 10.1149/1.2425526
J.K. Dawson, G. Long, W.E. Seddon, J.F. White, The kinetics and mechanism of the oxidation of zircaloy-2 at 350–500 °C Journal of Nuclear Materials. ,vol. 25, pp. 179- 200 ,(1968) , 10.1016/0022-3115(68)90044-5
R. E. Pawel, J. J. Campbell, Stress Generation during High‐Temperature Oxidation I . Oxygen Solution Effects Journal of The Electrochemical Society. ,vol. 116, pp. 828- 832 ,(1969) , 10.1149/1.2412071
R.A. Ploc, Transmission electron microscopy of thin (<2000 å) thermally formed ZrO2 films Journal of Nuclear Materials. ,vol. 28, pp. 48- 60 ,(1968) , 10.1016/0022-3115(68)90056-1
R. E. Pawel, J. V. Cathcart, J. J. Campbell, Stress Generation in Tantalum During Oxidation Journal of The Electrochemical Society. ,vol. 110, pp. 551- 557 ,(1963) , 10.1149/1.2425812
F.E. Buresch, F. Bollenrath, Über die mechanische beanspruchung von zirkonium und zircaloy-2 durch die korrosionsschicht Journal of Nuclear Materials. ,vol. 24, pp. 270- 280 ,(1967) , 10.1016/0022-3115(67)90200-0
R. E. Pawel, The Estimation of Bending Stresses from Flexure Measurements Journal of The Electrochemical Society. ,vol. 116, pp. 1144- 1146 ,(1969) , 10.1149/1.2412242
J. Paul Pemsler, Diffusion of Oxygen in Zirconium and Its Relation to Oxidation and Corrosion Journal of The Electrochemical Society. ,vol. 105, pp. 315- 322 ,(1958) , 10.1149/1.2428837