Deformation-Induced Martensitic Transformation in Cu-Zr-Zn Bulk Metallic Glass Composites
作者： Dianyu Wu , Kaikai Song , Chongde Cao , Ran Li , Gang Wang
DOI: 10.3390/MET5042134
关键词:
摘要: … Their average yield stress is 819 ± 60 MPa and 839 ± 200 MPa, while their fracture strength is 1821 ± 75 MPa and 1772 ± 120 MPa, respectively (Figure 4a and Table 1). Furthermore, …
mdpi.com
core.ac.uk 
sci-hub.se 参考文章(53)
Akihisa Inoue, Akira Takeuchi, Recent Progress in Bulk Glassy Alloys Materials Transactions. ,vol. 43, pp. 1892- 1906 ,(2002) , 10.2320/MATERTRANS.43.1892
BA Sun, WH Wang, The fracture of bulk metallic glasses Progress in Materials Science. ,vol. 74, pp. 211- 307 ,(2015) , 10.1016/J.PMATSCI.2015.05.002
F.A. Javid, N. Mattern, M. Samadi Khoshkhoo, M. Stoica, S. Pauly, J. Eckert, Phase formation of Cu50−xCoxZr50 (x = 0–20 at.%) alloys: Influence of cooling rate Journal of Alloys and Compounds. ,vol. 590, pp. 428- 434 ,(2014) , 10.1016/J.JALLCOM.2013.12.138
G. S. Firstov, J. Van Humbeeck, Yu. N. Koval, Peculiarities of the martensitic transformation in ZrCu intermetallic compound - potential high temperature SMA Le Journal de Physique IV. ,vol. 11, pp. Pr8- 481 ,(2001) , 10.1051/JP4:2001880
Dmitri Louzguine-Luzgin, Larissa Louzguina-Luzgina, Alexander Churyumov, Mechanical Properties and Deformation Behavior of Bulk Metallic Glasses Metals. ,vol. 3, pp. 1- 22 ,(2012) , 10.3390/MET3010001
Ilkay Kalay, Matthew J. Kramer, Ralph E. Napolitano, Crystallization Kinetics and Phase Transformation Mechanisms in Cu 56 Zr 44 Glassy Alloy Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 46, pp. 3356- 3364 ,(2015) , 10.1007/S11661-015-2921-5
KK Song, S Pauly, BA Sun, J Tan, M Stoica, U Kühn, J Eckert, None, Correlation between the microstructures and the deformation mechanisms of CuZr-based bulk metallic glass composites AIP Advances. ,vol. 3, pp. 012116- 012116 ,(2013) , 10.1063/1.4789516
H. Choi-Yim, R.D. Conner, F. Szuecs, W.L. Johnson, Processing, microstructure and properties of ductile metal particulate reinforced Zr57Nb5Al10Cu15.4Ni12.6 bulk metallic glass composites Acta Materialia. ,vol. 50, pp. 2737- 2745 ,(2002) , 10.1016/S1359-6454(02)00113-1
G. Wang, S. Pauly, S. Gorantla, N. Mattern, J. Eckert, Plastic Flow of a Cu50Zr45Ti5 Bulk Metallic Glass Composite Journal of Materials Science & Technology. ,vol. 30, pp. 609- 615 ,(2014) , 10.1016/J.JMST.2014.05.003
J.W. Qiao, A.C. Sun, E.W. Huang, Y. Zhang, P.K. Liaw, C.P. Chuang, Tensile deformation micromechanisms for bulk metallic glass matrix composites: From work-hardening to softening Acta Materialia. ,vol. 59, pp. 4126- 4137 ,(2011) , 10.1016/J.ACTAMAT.2011.03.036