Fatigue Modeling for Elastic Materials With Statistically Distributed Defects
作者： Ilya I. Kudish
DOI: 10.1115/1.2722771
关键词:
摘要: … fatigue cracks in bearings is oxide inclusions. In clean steels, … , fatigue cracks originate at different material defects which, … of fatigue life prediction can be treated as small fatigue cracks (…
asme.org
sci-hub.se 参考文章(22)
Han C. Wu, C. C. Yang, On the Influence of Strain-Path in Multiaxial Fatigue Failure Journal of Engineering Materials and Technology. ,vol. 109, pp. 107- 113 ,(1987) , 10.1115/1.3225948
Y MURAKAMI, S KODAMA, S KONUMA, Quantitative evaluation of effects of non-metallic inclusions on fatigue strength of high strength steels. I: Basic fatigue mechanism and evaluation of correlation between the fatigue fracture stress and the size and location of non-metallic inclusions International Journal of Fatigue. ,vol. 11, pp. 291- 298 ,(1989) , 10.1016/0142-1123(89)90054-6
Shigeo Shimizu, Fatigue Limit Concept and Life Prediction Model for Rolling Contact Machine Elements Tribology Transactions. ,vol. 45, pp. 39- 46 ,(2002) , 10.1080/10402000208982519
Ilya I. Kudish, Kenneth W. Burris, Modern State of Experimentation and Modeling in Contact Fatigue Phenomenon: Part II—Analysis of the Existing Statistical Mathematical Models of Bearing and Gear Fatigue Life. New Statistical Model of Contact Fatigue Tribology Transactions. ,vol. 43, pp. 293- 301 ,(2000) , 10.1080/10402000008982343
S. Ya. Yarema, Methodology of determining the characteristics of the resistance to crack development (crack resistance) of materials in cyclic loading Soviet Materials Science. ,vol. 17, pp. 371- 380 ,(1982) , 10.1007/BF00723893
Shao Eryu, Huang Xingyuan, Wang Changsheng, Zhu Yaomin, Chen Qing, A Method of Detecting Rolling Contact Crack Initiation and the Establishment of Crack Propagation Curves Tribology Transactions. ,vol. 31, pp. 6- 11 ,(1988) , 10.1080/10402008808981792
Ilya I. Kudish, A New Statistical Model of Contact Fatigue Tribology Transactions. ,vol. 43, pp. 711- 721 ,(2000) , 10.1080/10402000008982400
C. Q. Bowles, J. Schijve, The role of inclusions in fatigue crack initiation in an aluminum alloy International Journal of Fracture. ,vol. 9, pp. 171- 179 ,(1973) , 10.1007/BF00041859
N. Hasebe, S. Inohara, Stress analysis of a semi-infinite plate with an oblique edge crack Ingenieur-Archiv. ,vol. 49, pp. 51- 62 ,(1980) , 10.1007/BF00536598
M. Isida, Stress-Intensity Factors for the Tension of an Eccentrically Cracked Strip Journal of Applied Mechanics. ,vol. 33, pp. 674- 675 ,(1966) , 10.1115/1.3625138