Experimental determination of time taken for openly exposed metal surfaces to dry
作者： I. S. Cole , W. D. Ganther
关键词:
摘要: Abstract The time taken for wetness sensors on zinc plates, openly exposed to the atmosphere, dry was analysed at four sites in southern Australia. cover a range of environmental conditions from inland marine. A number typical drying patterns were observed, and it found that these could be related severity probable presence various salt contaminants. Therefore, marine site frequently slow (>4 h) appeared controlled by salts with low deliquescent relative humidity (DRH) such as MgCl2. In contrast, generally more rapid, which consistent either clean surface or high DRH NaCl. present paper presents histograms rate each relationship between distributions is discussed. relevance study modelling...
sci-hub.se 参考文章(14)
Shoji Kobayashi, Michihiko Hayakawa, Beam Controllable Headlighting System SAE transactions. ,vol. 100, pp. 1170- 1185 ,(1991) , 10.4271/910829
I.S. Cole, R. Holgate, P. Kao, W. Ganther, The rate of drying of moisture from a metal surface and its implication for time of wetness Corrosion Science. ,vol. 37, pp. 455- 465 ,(1995) , 10.1016/0010-938X(94)00146-W
Gamal A. EL-Mahdy, Kwang B. Kim, AC impedance study on the atmospheric corrosion of aluminum under periodic wet-dry conditions Electrochimica Acta. ,vol. 49, pp. 1937- 1948 ,(2004) , 10.1016/J.ELECTACTA.2003.12.022
I. S. Cole, W. D. Ganther, D. A. Paterson, A. Bradbury, Experimental studies on dependence of surface temperatures of exposed metal plates on environmental parameters Corrosion Engineering Science and Technology. ,vol. 40, pp. 328- 336 ,(2005) , 10.1179/174327805X79548
A. Nishikata, Y. Ichihara, T. Tsuru, An application of electrochemical impedance spectroscopy to atmospheric corrosion study Corrosion Science. ,vol. 37, pp. 897- 911 ,(1995) , 10.1016/0010-938X(95)00002-2
I. S. Cole, D. A. Paterson, W. D. Ganther, Holistic model for atmospheric corrosion Part 1 - Theoretical framework for production, transportation and deposition of marine salts Corrosion Engineering Science and Technology. ,vol. 38, pp. 129- 134 ,(2003) , 10.1179/147842203767789203
A.K. Neufeld, I.S. Cole, A.M. Bond, S.A. Furman, The initiation mechanism of corrosion of zinc by sodium chloride particle deposition Corrosion Science. ,vol. 44, pp. 555- 572 ,(2002) , 10.1016/S0010-938X(01)00056-7
R.P.Vera Cruz, A. Nishikata, T. Tsuru, Pitting corrosion mechanism of stainless steels under wet-dry exposure in chloride-containing environments Corrosion Science. ,vol. 40, pp. 125- 139 ,(1998) , 10.1016/S0010-938X(97)00124-8
I.S. Cole, D. Lau, D.A. Paterson, Holistic model for atmospheric corrosion Part 6 – From wet aerosol to salt deposit Corrosion Engineering Science and Technology. ,vol. 39, pp. 209- 218 ,(2004) , 10.1179/147842204X2880
Gamal Ahmed El-Mahdy, Atsushi Nishikata, Tooru Tsuru, Electrochemical corrosion monitoring of galvanized steel under cyclic wet–dry conditions Corrosion Science. ,vol. 42, pp. 183- 194 ,(2000) , 10.1016/S0010-938X(99)00057-8