KUHN‐MARK‐HOUWINK‐SAKURADA relations and unperturbed dimensions of poly(di‐n‐alkyl itaconates)

摘要: KUHN-MARK-HOUWINK-SAKURADA relations for poly(dimethyl-, diethyl-, di-n-propyl-, di-n-butyl-, di-n-hexyl-, di-n-octyl-, di-n-decyl-, and di-n-undecyl itaconate) were established in toluene at 25°C. The decreasing exponent a from 0.80 to 0.61, going lower higher members of the series, reflects solvent power toluene. Observed high molecular weights polymers are disagreement with formerly assumed strong chain transfer monomer propagation step. σ-parameters, evaluated according KURATA-STOCKMAYER extrapolation procedure, within limits 1.98 3.50, indicate progressively increasing steric hindrance free rotation this polymer homologueous series. KUHN-MARK-HOUWINK-SAKURADA-Gleichungen wurden fur Poly-(dimethyl-, diathyl-, di-n-decyl- und di-n-undecylitaconat) Toluol bei 25°C bestimmt. Die von den niederen zu hoheren Gliedern der Polymerenreihe 0,80 bis 0,61 abnehmenden Werte des Exponenten geben das abnehmende Losungsvermogen wieder. beobachteten hohen Molekulargewichte Polymeren stehen im Widerspruch fruher vermuteten starken Kettenubertragung durch Monomere radikalischen Polymerisation. Grose nach KURATA-STOCKMAYERschen Extrapolationsmethode bestimmten σ-Parameter Bereich 1,98 3,50 steht Zusammenhang mit stark zunehmenden sterischen Hinderung freien Drehbarkeit diese polymerhomologe Reihe.