On a damage mesomodel for laminates: micro–meso relationships, possibilities and limits
作者： P. Ladevèze , G. Lubineau
DOI: 10.1016/S0266-3538(01)00109-9
关键词:
摘要: The damage mesomodel for laminates (DML) which has been developed over the past 15 years (in particular at Cachan) is revisited, considering numerous pieces of work, both experimental and theoretical, that have carried out in micromechanics. This a first attempt to connect completely micromechanics mesomechanics laminates.
elsevier.com
sci-hub.se 参考文章(26)
P. Ladevèze, X. Aubard, C. Cluzel, L. Guitard, Damage and fracture modeling of 4D CC composites Studies in Applied Mechanics. ,vol. 46, pp. 351- 367 ,(1998) , 10.1016/S0922-5382(98)80052-4
R. Talreja, Damage mechanics of composite materials Elsevier. ,(1994)
JA Nairn, P Zoller, The Development of Residual Thermal Stresses in Amorphous and Semicrystalline Thermoplastic Matrix Composites ASTM International. ,(1987) , 10.1520/STP24386S
P LADEVEZE, E LEDANTEC, Damage modelling of the elementary ply for laminated composites Composites Science and Technology. ,vol. 43, pp. 257- 267 ,(1992) , 10.1016/0266-3538(92)90097-M
Roberts Joffe, Janis Varna, Analytical modeling of stiffness reduction in symmetric and balanced laminates due to cracks in 90° layers Composites Science and Technology. ,vol. 59, pp. 1641- 1652 ,(1999) , 10.1016/S0266-3538(99)00025-1
O. Allix, P. Ladevèze, Interlaminar interface modelling for the prediction of delamination Composite Structures. ,vol. 22, pp. 235- 242 ,(1992) , 10.1016/0263-8223(92)90060-P
A. Parvizi, J. E. Bailey, On multiple transverse cracking in glass fibre epoxy cross-ply laminates Journal of Materials Science. ,vol. 13, pp. 2131- 2136 ,(1978) , 10.1007/BF00541666
Olivier Allix, Nadia Bahlouli, Christophe Cluzel, Lionel Perret, Modelling and identification of temperature-dependent mechanical behaviour of the elementary ply in carbon/epoxy laminates Composites Science and Technology. ,vol. 56, pp. 883- 888 ,(1996) , 10.1016/0266-3538(96)00036-X
X.-F Zhou, J.A Nairn, H.D Wagner, Fiber–matrix adhesion from the single-fiber composite test: nucleation of interfacial debonding Composites Part A-applied Science and Manufacturing. ,vol. 30, pp. 1387- 1400 ,(1999) , 10.1016/S1359-835X(99)00043-3
Janis Varna, Roberts Joffe, NV Akshantala, Ramesh Talreja, Damage in composite laminates with off-axis plies Composites Science and Technology. ,vol. 59, pp. 2139- 2147 ,(1999) , 10.1016/S0266-3538(99)00070-6