摘要: Abstract Commercial and pure iron-silicon alloy (3.74 to 4.0 % Si) sheet test pieces were strained below into the Luders' extension examined under microscope. Theories on origin of slip assessed from observations made nucleation propagation slip. The metallographic evidence favours at grain boundaries supports Hall-Petch theory grain.