Issues in Predicting Long-Term Environmental Degradation of Fiber-Reinforced Plastics
作者： Aaron Barkatt
关键词:
摘要: … matrices exhibit viscoelastic behavior. At nearambient … fiber failure, whereas at elevated temperature and high moisture … not taken from the actual components used in a particular project …
docuri.com 参考文章(50)
L. Prian, A. Barkatt, Degradation mechanism of fiber-reinforced plastics and its implications to prediction of long-term behavior Journal of Materials Science. ,vol. 34, pp. 3977- 3989 ,(1999) , 10.1023/A:1004647511910
HL McManus, RA Cunningham, Materials and Mechanics Analyses of Durability Tests for High-Temperature Polymer Matrix Composites ASTM special technical publications. pp. 1- 17 ,(1997) , 10.1520/STP11364S
L Prian, R Pollard, R Shan, CW Mastropietro, TR Gentry, LC Bank, A Barkatt, Use of Thermogravimetric Analysis to Develop Accelerated Test Methods to Investigate Long-Term Environmental Effects on Fiber-Reinforced Plastics ASTM special technical publications. pp. 206- 222 ,(1997) , 10.1520/STP11376S
R Ohtani, T Kitamura, Y Uematsu, M Hojo, Mode I Delamination of Carbon Fiber Reinforced Thermoplastic Polymer Under Static and Cyclic Creep at Elevated Temperatures ASTM International. ,(1993) , 10.1520/STP18047S
D Choqueuse, P Davies, F Mazéas, R Baizeau, Aging of composites in water: Comparison of five materials in terms of absorption kinetics and evolution of mechanical properties ASTM special technical publications. pp. 73- 96 ,(1997) , 10.1520/STP11369S
Y Arslanian, PJ Hogg, Measurement of Stress Corrosion Crack Growth in Sheet Molding Compounds ASTM International. ,(1993) , 10.1520/STP18046S
TK O'Brien, SA Salpekar, Scale effects on the transverse tensile strength of graphite epoxy composites ASTM International. ,(1992) , 10.1520/STP12618S
G. Maier, H. Ott, H. Kreil, R. Stelter, Testing of wet fibre-reinforced plastics at elevated temperatures Composites. ,vol. 20, pp. 467- 470 ,(1989) , 10.1016/0010-4361(89)90216-4
F. R. Jones, J. W. Rock, A. R. Wheatley, The long term durability of stressed GRP in acidic environments Journal of Materials Science Letters. ,vol. 2, pp. 519- 521 ,(1983) , 10.1007/BF00721471
T.P. Skourlis, R.L. McCullough, The effect of temperature on the behavior of the interphase in polymeric composites Composites Science and Technology. ,vol. 49, pp. 363- 368 ,(1993) , 10.1016/0266-3538(93)90068-R