New evidence for GP zones in binary AlLi alloys
作者： J.M. Papazian , C. Sigli , J.M. Sanchez
DOI: 10.1016/0036-9748(86)90126-2
关键词:
摘要: Abstract The DSC results described above are thought to present a relatively complete and persuasive picture of the characteristics an AlLi phase which is metastable with respect δ′. not immediately after quenching; it appears at room temperature kinetics that similar those GP zones in other Al base alloys, dissolves 75–150°C range enthalpy typical zones, its dissolution also zones. measurements artifact caused by δ′, significantly more stable probably present. Finally, existence was predicted independently on sound theoretical grounds. According results, optimum conditions for observation would be long-term aging 2 2.5 wt% alloy 50 75°C region; TEM examinations such samples currently underway.
elsevier.com
sci-hub.se 参考文章(6)
C. Sigli, J.M. Sanchez, Theoretical description of phase equilibrium in binary alloys Acta Metallurgica. ,vol. 33, pp. 1097- 1104 ,(1985) , 10.1016/0001-6160(85)90203-2
D. B. Williams, J. W. Edington, The Precipitation of δ′ (Al3Li) in Dilute Aluminium–Lithium Alloys Metal science. ,vol. 9, pp. 529- 532 ,(1975) , 10.1179/030634575790445143
E.S. Balmuth, Particle size determination in an Al-3Li alloy using DSC Scripta Metallurgica. ,vol. 18, pp. 301- 304 ,(1984) , 10.1016/0036-9748(84)90440-X
John M. Papazian, A calorimetric study of precipitation in aluminum alloy 2219 Metallurgical Transactions A. ,vol. 12, pp. 269- 280 ,(1981) , 10.1007/BF02655200
John M. Papazian, Calorimetric Studies of Precipitation and Dissolution Kinetics in Aluminum Alloys 2219 and 7075 Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science. ,vol. 13, pp. 761- 769 ,(1982) , 10.1007/BF02642389
S.F. Baumann, D.B. Williams, Effects of capillarity and coherency on δ' (Al3Li) precipitation in dilute AlLi alloys at low undercoolings Acta Metallurgica. ,vol. 33, pp. 1069- 1078 ,(1985) , 10.1016/0001-6160(85)90200-7