Cerium-zirconium mixed oxide and method for manufacturing the same
作者： Hiroshi Kodama , Hiroshi Okamoto
DOI:
关键词:
摘要: A cerium-zirconium mixed oxide with improved heat resistance of the specific surface area at a high temperature (1000° C.) is provided along manufacturing method therefor. This comprises spherical particles 5 to 20 nm in size and rodlike diameter 150 length, preferably has pore volume 0.3 cm 3 /g or more 35 m 2 after hours treatment 1000° C.
lens.org 参考文章(15)
Kimio Ouchi, Yoshichika Umemoto, Toshio Nakatani, Zirconium- and cerium-based mixed oxide and method of production thereof ,(2000)
Gavin Edwards, Ian Chisem, Yasuhide Takao, Colin Norman, Process for preparing zirconium-cerium-based mixed oxides ,(2002)
Koji Matsui, Zirconia fine powder and method for its production ,(1997)
Jean-Yves Chane-Ching, Frederic Cobo, Method for preparing a mesostructured material from particles with nanometric dimensions ,(2000)
Toshio Kandori, Hideo Sobukawa, Akihiko Suda, Masahiro Sugiura, Hiroshi Hirayama, Mareo Kimura, Yoshio Ukyo, Tadashi Suzuki, Yasuo Ikeda, Solid solution particle of oxides, a process for producing the same and a catalyst for purifying exhaust gases ,(1996)
Shinichi Takeshima, Process for production of compound oxides ,(2004)
Antonio.L Quinelato, Elson Longo, Leinig A Perazolli, José A Varela, Effect of ceria content on the sintering of ZrO2 based ceramics synthesized from a polymeric precursor Journal of the European Ceramic Society. ,vol. 20, pp. 1077- 1084 ,(2000) , 10.1016/S0955-2219(99)00269-1
Hiroshi c o Daiichi Kegenso Okamoto, Zirconia porous body and manufacturing method thereof ,(2005)
Helmut Dr. Scharf, Process for the preparation of Zirconium dioxide powder ,(1990)