Fatigue Behavior of Aramid Fiber Reinforced Rubber Matrix Sealing Composites
作者： Boqin Gu , Xiaoming Yu , Bin Zhang
DOI: 10.1007/S12221-021-0486-Z
关键词:
摘要: This paper presents an experimental and theoretical study of aramid fiber reinforced rubber sealing composites (AFRC). The fatigue performance AFRC with different stress amplitudes mass fractions was tested, the residual strength after cycles conducted. fracture morphology samples fractions, were observed by scanning electron microscope (SEM), damage modes discussed. results analyzed predicted life model, stiffness model model. It found that agreed well measured results, which indicated proposed gave advantage in evaluating behavior without further morphological experiments.
springer.com
sci-hub.st 参考文章(28)
KENNETH L. REIFSNIDER, Damage and Damage Mechanics Composite Materials Series. ,vol. 4, pp. 11- 77 ,(1991) , 10.1016/B978-0-444-70507-5.50006-8
Bin Zhang, Xiaoming Yu, Boqin Gu, Micromechanical modeling of large deformation in sepiolite reinforced rubber sealing composites under transverse tension Polymer Composites. ,vol. 38, pp. 381- 388 ,(2017) , 10.1002/PC.23596
J.N. Yang, L.J. Lee, D.Y. Sheu, Modulus reduction and fatigue damage of matrix dominated composite laminates Composite Structures. ,vol. 21, pp. 91- 100 ,(1992) , 10.1016/0263-8223(92)90044-D
Alberto D’Amore, Massimiliano Giorgio, Luigi Grassia, Modeling the residual strength of carbon fiber reinforced composites subjected to cyclic loading International Journal of Fatigue. ,vol. 78, pp. 31- 37 ,(2015) , 10.1016/J.IJFATIGUE.2015.03.012
Fuqiang Wu, WeiXing Yao, A fatigue damage model of composite materials International Journal of Fatigue. ,vol. 32, pp. 134- 138 ,(2010) , 10.1016/J.IJFATIGUE.2009.02.027
W.X. Yao, N. Himmel, A new cumulative fatigue damage model for fibre-reinforced plastics Composites Science and Technology. ,vol. 60, pp. 59- 64 ,(2000) , 10.1016/S0266-3538(99)00100-1
W. Hwang, K.S. Han, Fatigue of Composites—Fatigue Modulus Concept and Life Prediction Journal of Composite Materials. ,vol. 20, pp. 154- 165 ,(1986) , 10.1177/002199838602000203
L.J. Lee, J.N. Yang, D.Y. Sheu, Prediction of fatigue life for matrix-dominated composite laminates Composites Science and Technology. ,vol. 46, pp. 21- 28 ,(1993) , 10.1016/0266-3538(93)90077-T
Z. Hashin, A. Rotem, A Fatigue Failure Criterion for Fiber Reinforced Materials. Journal of Composite Materials. ,vol. 7, pp. 448- 464 ,(1973) , 10.1177/002199837300700404
D. Revuelta, J. Cuartero, A. Miravete, R. Clemente, A new approach to fatigue analysis in composites based on residual strength degradation Composite Structures. ,vol. 48, pp. 183- 186 ,(2000) , 10.1016/S0263-8223(99)00093-8