THE TERNARY ALLOY SYSTEM: ALUMINIUM–LEAD–SILVER

摘要: 1. The area of partial miscibility for the ternary system, aluminium–lead–silver, has been determined by thermal and chemical analysis. It is found to extend from binary system aluminium–lead alloys containing a maximum 85.58% silver 4.71% lead weight.2. temperatures separation solid phase, bounding this area, have fall at first with addition aluminium–lead, until temperature 548.5 °C. reached. This solidification alloy that contains aluminium in their eutectic proportions, plus saturation lead. then increases about 736° 80% 14% does not coincide summit mutual solubility curve but lies well right it.3. No compounds found.4. practically coincides silver–lead.5. As far as can be determin...