The Effect of Cold Work in Metals on Powder Pattern Intensities
作者： B. L. Averbach , B. E. Warren
DOI: 10.1063/1.1698276
关键词:
摘要: Using crystal monochromated Cu Kα‐radiation and a Geiger counter spectrometer, integrated intensity measurements have been made for powder samples of cold‐worked annealed α‐brass. The effect cold work is to increase the strong lines make practically no change in weak lines. presumably due reduction extinction. Measurements were (400) reflection on sample an held at high temperature demonstrate difference between effects vibration.
scitation.org
harvard.edu
aip.org
sci-hub.se 参考文章(4)
Charles S. Barrett, Structure of Metals ,(2007)
Charless S. Smith, E. E. Stickley, The Width of X-Ray Diffraction Lines From Cold-Worked Tungsten andα-Brass Physical Review. ,vol. 64, pp. 191- 198 ,(1943) , 10.1103/PHYSREV.64.191
A. R. STOKES, K. J. PASCOE, H. LIPSON, X-Ray Evidence of the Nature of Cold Work in Metals Nature. ,vol. 151, pp. 137- 137 ,(1943) , 10.1038/151137A0
G W Brindley, P Ridley, An X-ray study of lattice-distortion in rhodium Proceedings of the Physical Society. ,vol. 50, pp. 501- 518 ,(1938) , 10.1088/0959-5309/50/4/303