Effect of additions of TiC and Re on high temperature corrosion performance of cold sprayed Ni–20Cr coatings
作者： Harpreet Singh , Niraj Bala , Narinder Kaur , Sanjeev K. Sharma , Deuk Young Kim
DOI: 10.1016/J.SURFCOAT.2015.08.002
关键词:
摘要: … X-ray diffraction, surface and cross-sectional FE-SEM/EDS techniques were used to … coatings performed better than the uncoated steel; the better hot corrosion resistance of the coatings …
sci-hub.se 
researchgate.net 参考文章(33)
H. E. Evans, M. P. Taylor, Diffusion Cells and Chemical Failure of MCrAlY Bond Coats in Thermal-Barrier Coating Systems Oxidation of Metals. ,vol. 55, pp. 17- 34 ,(2001) , 10.1023/A:1010369024142
G. Calvarin, R. Molins, A. M. Huntz, Oxidation Mechanism of Ni—20Cr Foils and Its Relation to the Oxide-Scale Microstructure Oxidation of Metals. ,vol. 53, pp. 25- 48 ,(2000) , 10.1023/A:1004578513020
P. Niranatlumpong, C. B. Ponton, H. E. Evans, The Failure of Protective Oxides on Plasma-Sprayed NiCrAlY Overlay Coatings Oxidation of Metals. ,vol. 53, pp. 241- 258 ,(2000) , 10.1023/A:1004549219013
U. K. Chatterjee, S. K. Roy, S. K. Bose, Environmental Degradation of Metals ,(2001)
D.B. Lee, J.H. Ko, J.H. Yi, Characterization of Oxide Scales Formed on High-Velocity Oxyfuel-Sprayed Ni-Co-Cr-Al-Y + ReTa Coatings Journal of Thermal Spray Technology. ,vol. 14, pp. 315- 320 ,(2005) , 10.1361/105996305X59396
F.H. Stott, The role of oxidation in the wear of alloys Tribology International. ,vol. 31, pp. 61- 71 ,(1998) , 10.1016/S0301-679X(98)00008-5
Buta Singh Sidhu, S. Prakash, High-Temperature Oxidation Behavior of NiCrA1Y Bond Coats and Stellite-6 Plasma-Sprayed Coatings Oxidation of Metals. ,vol. 63, pp. 241- 259 ,(2005) , 10.1007/S11085-005-3203-1
T. Sundararajan, S. Kuroda, T. Itagaki, F. Abe, Steam Oxidation Resistance of Ni-Cr Thermal Spray Coatings on 9Cr-1Mo Steel. Part 2: 50Ni-50Cr. ISIJ International. ,vol. 43, pp. 104- 111 ,(2003) , 10.2355/ISIJINTERNATIONAL.43.104
Niraj Bala, Harpreet Singh, Satya Prakash, High Temperature Corrosion Behavior of Cold Spray Ni-20Cr Coating on Boiler Steel in Molten Salt Environment at 900 °C Journal of Thermal Spray Technology. ,vol. 19, pp. 110- 118 ,(2010) , 10.1007/S11666-009-9437-8
T.S. Sidhu, S. Prakash, R.D. Agrawal, Hot corrosion studies of HVOF sprayed Cr3C2–NiCr and Ni–20Cr coatings on nickel-based superalloy at 900 °C Surface & Coatings Technology. ,vol. 201, pp. 792- 800 ,(2006) , 10.1016/J.SURFCOAT.2005.12.030