Effect of irradiation on corrosion of 304 nuclear grade stainless steel in simulated PWR primary water
作者： Ping Deng , Qunjia Peng , En-Hou Han , Wei Ke , Chen Sun
DOI: 10.1016/J.CORSCI.2017.08.010
关键词:
摘要: … corrosion of 304 nuclear grade (NG) SS in simulated primary water of pressurized water reactor … dose to the overall corrosion, as well as the RIS to localized corrosion at the grain …
sci-hub.se 参考文章(43)
Yaolei Han, Jinna Mei, Qunjia Peng, En-Hou Han, Wei Ke, Effect of electropolishing on corrosion of Alloy 600 in high temperature water Corrosion Science. ,vol. 98, pp. 72- 80 ,(2015) , 10.1016/J.CORSCI.2015.05.026
Loïc Marchetti, Stéphane Perrin, Fanny Jambon, Michèle Pijolat, Corrosion of nickel-base alloys in primary medium of pressurized water reactors: New insights on the oxide growth mechanisms and kinetic modelling Corrosion Science. ,vol. 102, pp. 24- 35 ,(2016) , 10.1016/J.CORSCI.2015.09.001
M. D. McMurtrey, G. S. Was, Role of Slip Behavior in the Irradiation Assisted Stress Corrosion Cracking in Austenitic Steels 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors 2011. pp. 1383- 1395 ,(2011) , 10.1007/978-3-319-48760-1_85
Zhijie Jiao, Gary Was, Oxidation of a Proton-Irradiated 316 Stainless Steel in Simulated BWR NWC Environment Proceedings of the 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems — Water Reactors. pp. 1329- 1338 ,(2011) , 10.1007/978-3-319-48760-1_81
Sergio Lozano-Perez, Karen Kruska, Ilya Iyengar, Takumi Terachi, Takuyo Yamada, The role of cold work and applied stress on surface oxidation of 304 stainless steel Corrosion Science. ,vol. 56, pp. 78- 85 ,(2012) , 10.1016/J.CORSCI.2011.11.021
Koji FUKUYA, Morihito NAKANO, Katsuhiko FUJII, Tadahiko TORIMARU, Role of Radiation-Induced Grain Boundary Segregation in Irradiation Assisted Stress Corrosion Cracking Journal of Nuclear Science and Technology. ,vol. 41, pp. 594- 600 ,(2004) , 10.1080/18811248.2004.9715522
J. Robertson, The mechanism of high temperature aqueous corrosion of steel Corrosion Science. ,vol. 29, pp. 1275- 1291 ,(1989) , 10.1016/0010-938X(89)90120-0
Stéphane Perrin, Loic Marchetti, Cécilie Duhamel, Mohamed Sennour, François Jomard, Influence of Irradiation on the Oxide Film Formed on 316 L Stainless Steel in PWR Primary Water Oxidation of Metals. ,vol. 80, pp. 623- 633 ,(2013) , 10.1007/S11085-013-9401-3
Z. Jiao, G.S. Was, Impact of localized deformation on IASCC in austenitic stainless steels Journal of Nuclear Materials. ,vol. 408, pp. 246- 256 ,(2011) , 10.1016/J.JNUCMAT.2010.10.087
Kale J. Stephenson, Gary S. Was, Crack initiation behavior of neutron irradiated model and commercial stainless steels in high temperature water Journal of Nuclear Materials. ,vol. 444, pp. 331- 341 ,(2014) , 10.1016/J.JNUCMAT.2013.10.008