Ceramic temperature stabilization body, and method of making same
作者： Waltraud Werdecker , Fritz Aldinger
DOI:
关键词:
摘要: The temperature stabilization body is made of pulverized aluminum nitride with a first additive present between 0.05% to 2%, and grain size under 1 micrometer, second from 0.1% 10% an oxide, preferably yttrium at about 1%--all precentages by weight, in which the mixture ground ceramic ball mill not over 0.1 mm, subjected cold isostatic pressure order 2500 bar form green, pressed body, then sintered sintering 1750° C. 2000° heat conductivity densely will be least 140 W/m °K., twice as much can obtained, being non-toxic subject creep temperatures up 1700°
lens.org 参考文章(14)
Francis R. Corrigan, Polycrystalline cubic boron nitride abrasive and process for preparing same in the absence of catalyst ,(1979)
Camille A Lenie, Kenneth M Taylor, Refractory articles and method of making same ,(1959)
Francis R. Corrigan, Direct conversion process for making cubic boron nitride from pyrolytic boron nitride ,(1977)
Waltraud Werdecker, Fritz Aldinger, Richard Keilberth, Low-contamination AlN crucible for monocrystal pulling and method ,(1983)
Hiroshi Inoue, Katsutoshi Komeya, Method for manufacturing heat-resistant reinforced composite materials ,(1976)
Babl Albert, Geng Heinz, Preparation of hexagonal boron nitride ,(1967)
Hiroshi Inoue, Akihiko Tsuge, Katsutoshi Komeya, Sintered bodies of aluminum nitride ,(1982)
Kelly D. McHenry, Barry G. Koepke, Composite electronic substrate of alumina uniformly needled through with aluminum nitride ,(1980)
Toshihiko Ochiai, Mitsutoshi Hirano, Hiroshi Inoue, Pump member for molten metal ,(1973)
Cyril A. Morgan, Scott G. Arber, Oswald W.J. Young, Process for purification of refractory metal nitrides ,(1970)