On the anionic polymerization of styrene. Biphenyl-sodium a new initiator†

摘要: In contradiction to the results reported by SZWARC and co-workers it was found that a one-stage low tempertature polymerization of styrene with Nanaphthalene does not lead an extremely sharp molecular weight distribution. A narrow distribution chain lengths can however be obtained in two-stage polymerization. first stage initator is reacted completely small amount monomer at relatively high temperature. After cooling solution temperature rest added. On basis electrochemical considerations shown, Na-biphenyl as initiator, one step should yield monodisperse product. This confirmed through experiment which polymer Mw/Mn ratio 1.026 obtained. Die einstufige Tieftemperatur-Polymerisation von Styrol mit Na-Napthalin nach fuhrt nicht zu extrem scharfen Moleculargewichtsverteilung. Eine scharfe Verteilung der Kettenlangen last sich jedoch einer Zweistufenpolymerisation erzielen. Der Initiator wird dabei kleinen Menge des Monomeren bei relativ hohen Temperatur vollstandig umgesetzt und Rest Styrols Abkuhlung auf die Polymerisationstemperatur zugegeben. An Hand elektrochemischen Uberlegungen gezeigt, das Na-Biphenyl als einstufigen monodisperses Polystyrol erzielen lassen sollte. Die Einheitlichkeit diese Weise erhaltenen Polymeren ist, Bestatigung Therorie, einem Mw/Mn-Quotienten 1,026 auserordentlich gut.