The creep behaviour of aluminium-alumina (SAP) alloys
作者： P. Bonnet , H. Kellerer , G. Piatti , H.W. Schleicher
DOI: 10.1016/0036-9748(68)90245-7
关键词:
摘要: Abstract The creep behaviour of AlAl2O3 alloys has been studied at 450°C for times-to-rupture between 10 min. and 1000 h. Tests are concentrated mainly on SAP containing 7% oxide. results exhibit a relatively high scatter. In order to clarify the mechanism process density measurements have made samples in different zones. Electron micrographs prepared as well. On basis these tests can be related rate crack formation depending nature interface.
elsevier.com
sci-hub.se 参考文章(4)
H. Kellerer, G. Piatti, The influence of microporosity on the ductility of Al/Al2O3 alloys Journal of Materials Science. ,vol. 3, pp. 222- 224 ,(1968) , 10.1007/BF00585490
William D. Nix, Reply to comment on: “On the jogged screw dislocation model for steady state creep” Scripta Metallurgica. ,vol. 1, pp. 171- 172 ,(1967) , 10.1016/0036-9748(67)90039-7
Y. Ishida, D. McLean, The Formation and Growth of Cavities in Creep Metal Science Journal. ,vol. 1, pp. 171- 172 ,(1967) , 10.1179/MSC.1967.1.1.171
G.S Ansell, F.V Lenel, Criteria for yielding of dispersion-strengthened alloys Acta Metallurgica. ,vol. 8, pp. 612- 616 ,(1960) , 10.1016/0001-6160(60)90015-8