Evaluation Of Bis-GMA/MMA Resin Adhesion To Silica-Coated And Silanized Titanium
作者： Mervi Puska , Lippo Lassila , Pekka K. Vallittu , Jukka Seppälä , Jukka Matinlinna
关键词:
摘要: The effects of pH value and alcohol solvent type a silane solution on the bonding an experimental resin to silica-coated titanium (Ti) surface were studied. First, Ti surfaces underwent tribochemical Rocatec™ treatment followed by silanization with 3-methacryloxypropyltrimethoxysilane (MPS). Then, stubs based mixture bisphenol-A-glycidyl dimethacrylate methyl methacrylate bonded light-cured onto each (n = 6 per group). Two different solvents for MPS, namely iso-propanol (i-PrOH)/H2O ethanol (EtOH)/H2O used, at values 4.5, 5.0, 5.5, shear bond strengths tested both under dry storage conditions after water sorption induced accelerated aging (i.e. thermo-cycling). also re-determined solutions had been stored 4°C 15 weeks before step. For samples, ranged from 7.5 10.6 MPa (ANOVA, p < 0.05) when the...
hku.hk
brillonline.com 参考文章(36)
James G. Marsden, Organofunctional Silane Coupling Agents Springer, Boston, MA. pp. 536- 548 ,(1990) , 10.1007/978-1-4613-0671-9_31
J. P. Matinlinna, M. Özcan, L. V. J. Lassila, P. K. Vallittu, Applications Of Trialkoxysilanes In Dental Biomaterials: A Review Silanes and Other Coupling Agents, Volume 4. pp. 199- 216 ,(2007) , 10.1163/EJ.9789067644525.I-410.94
Irving Skeist, Handbook of adhesives ,(1977)
W.J. van Ooij, D.Q. Zhu, G. Prasad, S. Jayaseelan, Y. Fu, N. Teredesai, Silane based chromate replacements for corrosion control, paint adhesion, and rubber bonding Surface Engineering. ,vol. 16, pp. 386- 396 ,(2000) , 10.1179/026708400101517369
J.P. Matinlinna, L.V.J. Lassila, P.K. Vallittu, Evaluation of five dental silanes on bonding a luting cement onto silica-coated titanium Journal of Dentistry. ,vol. 34, pp. 721- 726 ,(2006) , 10.1016/J.JDENT.2006.01.005
Giuliana Tesoro, Yulong Wu, Silane coupling agents: the role of the organofunctional group Journal of Adhesion Science and Technology. ,vol. 5, pp. 771- 784 ,(1991) , 10.1163/156856191X00206
Eeva K. Viljanen, Mikael Skrifvars, Pekka K. Vallittu, Degree of conversion of a copolymer of an experimental monomer and methyl methacrylate for dental applications Journal of Applied Polymer Science. ,vol. 93, pp. 1908- 1912 ,(2004) , 10.1002/APP.20654
Y. Finer, J.P. Santerre, Influence of silanated filler content on the biodegradation of bisGMA/TEGDMA dental composite resins Journal of Biomedical Materials Research Part A. ,vol. 81, pp. 75- 84 ,(2007) , 10.1002/JBM.A.31004
Gina Gualtieri, Erik Erbe, Ted Clineff, Comparison of a new bisphenol-a-glycidyl dimethacrylate-based cortical bone void filler with polymethyl methacrylate European Spine Journal. ,vol. 10, ,(2001) , 10.1007/S005860100288
Mine Dündar, Mutlu Özcan, Bülent Gökçe, Erhan Çömlekoğlu, Fabiola Leite, Luiz Felipe Valandro, Comparison of two bond strength testing methodologies for bilayered all-ceramics Dental Materials. ,vol. 23, pp. 630- 636 ,(2007) , 10.1016/J.DENTAL.2006.05.004